| Category: | HDPE , High Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | UNIVAL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PvFc8s_UNIVAL-DMDA-6220-NT-7.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Complies with:
UNIVAL™ DMDA-6220 NT 7 High Density Polyethylene (HDPE) Resin is an antistat containing, multipurpose polymer designed for the high speed production of blow molded containers used to package household industrial chemicals (e.g., detergents, bleach, fabric softeners), toiletries and cosmetics (e.g., shampoos, creams, lotions, etc.), health and medicinal aids, and food products. In addition, it can be blow molded into other thin walled parts and houseware items, and also can be extruded into profiles. |
| General Information | |
|---|---|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.953 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 190°C/2.16 kg | 0.38 | g/10 min | ASTM D1238 |
| 190°C/21.6 kg | 33 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 100% Igepal, F50) | 60.0 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 62 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield | 26.9 | MPa | ASTM D638 |
| Fracture | 31.7 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 7.0 | % | ASTM D638 |
| Fracture | 1000 | % | ASTM D638 |
| Flexural Modulus - 2% Secant | 1050 | MPa | ASTM D790B |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Impact Strength 1 | 168 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 67.0 | °C | ASTM D648 |
| Brittleness Temperature | < -76.1 | °C | ASTM D746 |
| Vicat Softening Temperature | 129 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 131 | °C | Internal method |
| Peak Crystallization Temperature (DSC) | 119 | °C | Internal method |
| Additional Information |
|---|
| 根据 ASTM D 4976 进行基板模制和测试。 |
| Note Message | |
|---|---|
| 1 . | Type s |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200H TFE 15 | RTP Company | Nylon 66 | RTP |
| Mirakutoran® TPU H890FNAT | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| SILPURAN® 6000/40 A/B | Wacker Chemie AG | Silicone | SILPURAN® |
| BCC Resins BC 7062-2H | BCC Products Inc. | Epoxy | BCC Resins |
| Karina BLACK PVC COMPUND 850-48/ 1-D-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |