Trilliant™ HC HC6200-5001 XR Grey
| Category: | Nylon 12 , Polyamide 12 |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Trilliant™ HC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PuTXWO_Trilliant-HC-HC6200-5001-XR-Grey.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead of competition. When specified, Trilliant® compound may incorporate agency rated materials that meet USP Class IV, FDA or ISO 10993 testing requirements. This Trilliant® grade is a high density specialty compound featuring a sustainable material solution for radiation shielding and weighting & balancing applications. The composite material offers a high performance thermoplastic-based alternative to lead. This compound has densities similar to traditional metals and provides greater flexibility in design and processing. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 11.0 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.40 - 0.80 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 0.50 - 1.0 | % | ISO 527-2/50 |
| Flexural Modulus | 10000 | MPa | ISO 178 |
| Flexural Stress | 75.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 5.0 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 10 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 130 | °C | ISO 75-2/A |
| Thermal Conductivity 1 | 3.0 - 3.5 | W/m/K | ASTM E1461 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+3 | ohms | IEC 60093 |
| Additional Information |
|---|
| Shielding properties:Attenuation coefficient at 511 keV = 0.94cm-1Half Thickness at 511 keV = 0.74cm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Processing (Melt) Temp | 230 - 280 | °C | |
| Mold Temperature | 65.0 - 100 | °C |
| Note Message | |
|---|---|
| 1 . | Through Plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXUS PE HDPE-1062 | Nexus Resin Group, LLC. | HDPE | NEXUS PE |
| FLEXOMER™ ETS-9078 NT 7 | The Dow Chemical Company | VLDPE | FLEXOMER™ |
| Elastron® TPO T100.D60.N | Elastron USA, Inc. | TPO (POE) | Elastron® TPO |
| EMOPLEN® CP GFR 30 UV | EMAS Plastik San.Tic.AS. | PP Copolymer | EMOPLEN® |
| Horda E8201 | Horda Cable Compounds | PE, Unspecified | Horda |