Trithene® TU 8091
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Petroquimica Triunfo |
| Trademark: | Trithene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pt7tKL_Trithene-TU-8091.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Trithene®TU 8091 is a low density polyethylene material,. This product is available in Latin America,. Trithene®The main features of TU 8091 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.12 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, molding | 11.0 | MPa | ASTM D638 |
| Fracture, molding | 18.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 630 | % | ASTM D638 |
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.56 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| secant modulus | ASTM D882 | ||
| 5% secant, MD : 150 µm, blown film | 92.0 | MPa | ASTM D882 |
| 5% secant, TD : 150 µm, blown film | 91.0 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Broken, 150 µm, blown film | 20.0 | MPa | ASTM D882 |
| TD : Broken, 150 µm, blown film | 22.0 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Broken, 150 µm, blown film | 600 | % | ASTM D882 |
| TD : Broken, 150 µm, blown film | 740 | % | ASTM D882 |
| Dart Drop Impact (150 µm, Blown Film) | 400 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 150 µm, blown film | 440 | g | ASTM D1922 |
| TD : 150 µm, blown film | 720 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 150 µm, Blown Film) | 62 | ASTM D2457 | |
| Transmittance (150 µm) | 94.0 | % | ASTM D1003 |
| Haze (150 µm, Blown Film) | 13 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties taken from 150 µm blown film produced on a 50 mm extruder, L/D=25, die gap=1.0 mm, BUR=2.3:1Melt Mass-Flow Rate, ASTM D1238, 190°C/2.16 kg: 0.10 to 0.14 g/10 minDensity, ASTM D1505: 0.922 to 0.924 g/cm³Teor de Agente Anti-U.V., PTN-723-Q: 4750 to 5500 ppm |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 170 - 185 | °C | |
| Cylinder Zone 2 Temp. | 180 - 195 | °C | |
| Cylinder Zone 3 Temp. | 200 - 220 | °C |
| Extrusion instructions |
|---|
| Recommended Blow Up Ratio: 2-3:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-BR1 | Polymer Resources Ltd. | PC | PRL |
| ALCOM® PA66 910/1.1 CF20 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| ALTECH® PA66 A 2060/100 GF60 | ALBIS PLASTIC GmbH | Nylon 66 | ALTECH® PA66 |
| INSTRUC PSUGF30HF | Infinity LTL Engineered Compounds | PSU | INSTRUC |
| Sylvin 6234-90 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |