LNP™ THERMOCOMP™ RFB71S compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PsFEGm_LNP-THERMOCOMP-RFB71S-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP THERMOCOMP RFB71S is a compound based on Nylon 66 resin containing Glass Fiber, Glass Bead. Added features of this material include: Heat Stabilized. Also known as: LNP* THERMOCOMP* Compound RF-1008 HS MG Product reorder name: RFB71S |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow 1 | 0.70 to 0.90 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5800 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 99.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus 2 | 5000 | MPa | ISO 178 |
| Flexural Stress 3 | ISO 178 | ||
| -- 4 | 155 | MPa | |
| -- 5 | 90.0 | MPa |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength 6(23°C) | 4.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 7(23°C) | 25 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 8 | |||
| 0.45 MPa, Unannealed, 64.0 mm Span | 243 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 64.0 mm Span | 137 | °C | ISO 75-2/Af |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 60°C | 5.2E-5 | cm/cm/°C | |
| Transverse : 23 to 60°C | 7.3E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 282 to 304 | °C | |
| Mold Temperature | 93.3 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 2.0 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | Yield |
| 5 . | Break |
| 6 . | 80*10*4 |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sup-tech B9706 | Shanghai Suptech Engineering Plastics Co. Ltd. | Nylon 6 | Sup-tech |
| XENOY™ 2230 resin | SABIC Innovative Plastics | PC+PET | XENOY™ |
| Axiall PVC 8833 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| CPI PA6 40 Natural | CPI Binani, Inc. | Nylon 6 | CPI PA6 |
| Sylvin 9769-83 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |