Polyopt® BLS64
| Category: | Film, PS , PS Film |
| Manufacturer: | Suzhou OMAY Optical Materials Co., Ltd |
| Trademark: | Polyopt® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PrUL5z_Polyopt-BLS64.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Orange peel/Velvet, nature colour, Polystyrene (PS) |
| General Information | |
|---|---|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.20 to 0.60 | % | Internal Method |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 48.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2 |
| Flexural Modulus | 3150 | MPa | ISO 178 |
| Flexural Stress | 94.0 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 102 | °C | ISO 306 |
| Heat Distortion | 86 | °C | ISO 306 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60093 |
| Dielectric Constant | 3.70 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 55.0 to 65.0 | % | ASTM D1003 |
| Haze | > 95 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radiflam® A RV250 AF 375 NER | Radici Plastics | Nylon 66 | Radiflam® |
| Nypol® PA A3 G20 HS NTLA013 NR437 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Delta IPP 2507 | Delta Polymers | PP Copolymer | Delta |
| Forprene® 6NE001A45 | SO.F.TER. SPA | TPV | Forprene® |
| LG ABS XR410 | LG Chem Ltd. | ABS | LG ABS |