Cereplast Compostables® 2001
| Category: | PLA , Polylactic Acid |
| Manufacturer: | Cereplast, Inc. |
| Trademark: | Cereplast Compostables® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PrQ2Xe_Cereplast-Compostables-2001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Cereplast Compostables® resins are renewable, ecologically sound substitutes for petroleum-based plastic product, replacing nearly 100% of the petroleum-based additives used in traditional plastics. Cereplast Compostables® resins are using polymer and additives derived from starch and other renewable resources chemistry. These components are carefully blended together on state-of-the-art compounding equipments. All Cereplast Compostables® resins, including Compostable 2001, are certified as biodegradable and compostable in the United States and Europe, meeting BPI (Biodegradable Products Institute www.bpiworld.com) standards for compostability (ASTM6400D99, ASTM6868) and European Bioplastics Standards (EN13432). Compostable 2001 has been designed to have an excellent balance of toughness, rigidity and processability. Compostable 2001 can be processed on existing blow molding machines. Please see our processing guide for processing and material drying guidelines. This can be found at www.cereplast.com. Compostable 2001 have been specially designed for bottles, containers and similar type applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3240 | MPa | ASTM D638 |
| Tensile Strength (Break) | 55.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638 |
| Flexural Modulus | 2830 | MPa | ASTM D790 |
| Flexural Strength | 92.4 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 25 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 47.8 | °C | ASTM D648 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Cylinder Zone 1 Temp. | 154 - 174 | °C | |
| Cylinder Zone 2 Temp. | 163 - 171 | °C | |
| Cylinder Zone 3 Temp. | 166 - 182 | °C | |
| Adapter Temperature | 171 - 193 | °C | |
| Melt Temperature | 199 | °C | |
| Die Temperature | 171 - 193 | °C |
| Extrusion instructions |
|---|
| Mold Temperature: 50 to 80°FScrew Speed: 20 to100 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Braskem PP C765-15NA | Braskem Europe GmbH | PP Impact Copolymer | Braskem PP |
| ChronoThane™ P 80A | CardioTech International, Inc. | TPU-Polyether | ChronoThane™ |
| Flontech® FT-1-5 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Hostacom DKC 179N | LyondellBasell Industries | PP Alloy | Hostacom |
| Axiall PVC 1601 | Axiall Corporation | PVC, Flexible | Axiall PVC |