BJB Polyurethane TC-892 FR REV 1
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | BJB Enterprises, Inc. |
| Trademark: | BJB Polyurethane |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PrDhTs_BJB-Polyurethane-TC-892-FR-REV-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
This tough 80 Shore D Flame Retardant material is UL Listed with a flammability rating at 1/16 inch (1.6 mm). It’s great for hand casting or machine dispensing electronic enclosures, or any parts requiring flame retardant characteristics. The 20 to 25 minute work time exhibits very low shrinkage and exceptional physical properties. Also available in a variety of work times as TC-890, 891 and 894 FR REV 1.
|
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| UL File Number |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | ASTM D792 | ||
| -- 1 | 1.18 | g/cm³ | |
| -- | 1.30 | g/cm³ | |
| -- 2 | 1.33 | g/cm³ | |
| Specific Volume | 0.791 | cm³/g | |
| Shrinkage 3(1.27 cm) | Nil |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gel Time | 30.0 to 35.0 | min | |
| Work Time 4(25°C) | 20.0 to 25.0 | min |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 78 to 82 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1720 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 42.2 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | 21 | % | ASTM D638 |
| Flexural Modulus | 1940 | MPa | ASTM D790 |
| Flexural Strength | 69.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 31 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 85.6 | °C | |
| 1.8 MPa, Unannealed | 75.6 | °C | |
| Ball Pressure Test (75°C, 1.30 mm) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Test Method | |
|---|---|---|---|
| Dielectric Constant (1 MHz) | 3.24 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 0.014 | ASTM D150 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.59 mm) | V-0 | UL 94 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 70, Mix Ratio by Volume: 79 | ||
| Part B | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | ||
| Shelf Life | 26 | wk | |
| Thermoset Mix Viscosity | ASTM D2393 | ||
| 25°C 5 | 740 | cP | |
| 25°C 6 | 1450 | cP | |
| 25°C 7 | 325 | cP | |
| Demold Time (25°C) | 300 to 360 | min | |
| Post Cure Time (25°C) | 120 to 170 | hr |
| Note Message | |
|---|---|
| 1 . | Part A |
| 2 . | Part B |
| 3 . | 12x0.5x0.5 in |
| 4 . | 100g mass |
| 5 . | Mixed |
| 6 . | Part B |
| 7 . | Part A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nycast CP | Cast Nylons Ltd. | Nylon 6 | Nycast |
| Bergamid™ X BG6600-8047 RS BK001 | PolyOne Corporation | Nylon 66 | Bergamid™ |
| EPO-TEK® 323LP-LH Premium | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| Okirol® E-6F | DIOKI d.d. | PS (EPS) | Okirol® |
| Sylvin 9812-65 White 1514 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |