ALCUDIA® HDPE 5300-N
| Category: | HDPE, HMW , High Density (HMW) Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® HDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PqaW4R_ALCUDIA-HDPE-5300-N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 5502-E natural compound is an hexene copolymer of medium molecular weight apt for the extrusion of corrugated pipes for protection of cables, one or multilayered pipe. This product is supplied in natural colour but it can be easily coloured with pigments steady at processing temperature, using dry-colouring or masterbatch techniques ALCUDIA® 5502E is a high-density polyethylene copolymer of hexene, with high molecular weight. It is specially designed to make, by blow molding-extrusion, tanks for liquid detergents and chemicals. This grade contains stabilizers according to the end use of the item in order to reinforce the thermal stability. Good environmental stress cracking resistance can be obtained with ALCUDIA® 5502E due to its molecular weight and density. TYPICAL APPLICATIONS Packaging of non-aggressive liquid detergents and chemicals. Recommended melt temperature range from 180 to 200°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.954 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | ISO 1133 | ||
| 190°C/2.16 kg | 0.11 | g/10 min | |
| 190°C/21.6 kg | 11 | g/10 min | |
| 190°C/5.0 kg | 0.50 | g/10 min | |
| Environmental Stress-Cracking Resistance (10% Antarox CO-630, F50) | > 1000 | hr | ASTM D1693 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 60 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 35.0 | MPa | EN 638 |
| Tensile Strain (Break) | 800 | % | EN 638 |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Internal Pressure Resistance | EN 1555/12201 | ||
| 10 MPa : 20°C | > 4.2 | day | |
| 4.0 MPa : 80°C | > 41.7 | day | |
| 4.6 MPa : 80°C | > 6.9 | day |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxidation Induction Time (210°C) | > 20 | min | EN 728 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Long-Term Hydrostatic Strength - 50 years (20°C) 1 | > 8.00 | MPa | ISO TR 9080 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -118 | °C | ASTM D746 |
| Vicat Softening Temperature | 126 | °C | ASTM D1525 2 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 175 to 195 | °C | |
| Cylinder Zone 2 Temp. | 180 to 200 | °C | |
| Cylinder Zone 3 Temp. | 185 to 205 | °C | |
| Cylinder Zone 4 Temp. | 190 to 210 | °C | |
| Cylinder Zone 5 Temp. | 195 to 215 | °C | |
| Melt Temperature | 195 to 215 | °C |
| Note Message | |
|---|---|
| 1 . | Regression Curve |
| 2 . | Rate A (50°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Matrixx 75S5251 | The Matrixx Group, Inc. | Nylon 66 | Matrixx |
| DeWAL DW 224 | DeWAL Industries | PTFE | DeWAL |
| Electrafil® ABS SS16 FR BK | Techmer Engineered Solutions | ABS | Electrafil® |
| Hostacom DB273A | LyondellBasell Industries | TPO (POE) | Hostacom |
| LNP™ LUBRICOMP™ 9X06483 compound | SABIC Innovative Plastics | Nylon 46 | LNP™ LUBRICOMP™ |