Capilene® SE 50 E
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Carmel Olefins Ltd. |
| Trademark: | Capilene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | Pq7Mn5_Capilene-SE-50-E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CAPILENE ® SE 50 E is a low melt flow rate polypropylene heterophasic copolymer intended for extrusion applications. CAPILENE ® SE 50 E features: excellent impact strength even at low temperature, good stiffness and excellent processability. CAPILENE ® SE 50 E is suitable for: sheets, corrugated boards, profiles; injection molded technical items and blow molded containers. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 1.3 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 24.0 | MPa | ASTM D638 |
| Yield | 24.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 2 | 12 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- | 1150 | MPa | ASTM D790 |
| -- 3 | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| -20°C | 60 | J/m | ASTM D256 |
| 23°C | 550 | J/m | ASTM D256 |
| -20°C | 5.0 | kJ/m² | ISO 180 |
| 23°C | 35 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 85.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed | 73.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 150 | °C | ISO 306/A, ASTM D1525 4 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Witcom PA66 3A/2L1 | Witcom Engineering Plastics B.V. | Nylon 66 | Witcom PA66 |
| NOVAREX® M7026U | Mitsubishi Engineering-Plastics Corp | PC | NOVAREX® |
| APEX® 468 | Teknor Apex Company | PVC, Flexible | APEX® |
| INSPIRE™ 382 | Braskem Europe GmbH | PP Random Copolymer | INSPIRE™ |
| INNOPOL® PP CS 2-9301 | Inno-Comp Ltd. | PP Copolymer | INNOPOL® PP |