Nylene® 733

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Custom Resins Group
Trademark:	Nylene®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	Pq0efv_Nylene-733.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Highly impact modified nylon suitable for both molding and extrusion

Parts molded from 733 have excellent impact strength right out of the mold without post conditioning

Highlights include high stiffness and high strength

Cylinder temperatures should be in the 500-550°F range.

General Information
Additive	Impact Modifier
Features	Good Impact Resistance High Stiffness High Strength Impact Modified
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.08	g/cm³	ASTM D792
Molding Shrinkage - Flow	1.4	%	ASTM D955

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength (23°C)	72.4	MPa	ASTM D638
Tensile Elongation (Break, 23°C)	200	%	ASTM D638
Flexural Modulus (23°C)	2070	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact			ASTM D256
-40°C	160	J/m
23°C	850	J/m

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	61.1	°C	ASTM D648
Peak Melting Temperature	218	°C	ASTM D3418

Injection	Nominal Value	Unit
Rear Temperature	260 to 288	°C
Middle Temperature	260 to 288	°C
Front Temperature	260 to 288	°C

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	260 to 288	°C
Cylinder Zone 2 Temp.	260 to 288	°C
Cylinder Zone 3 Temp.	260 to 288	°C
Cylinder Zone 4 Temp.	260 to 288	°C
Cylinder Zone 5 Temp.	260 to 288	°C

Resin Grade	Manufacturer	Category	Trademark
Milastomer™ 8030NHS	Mitsui Chemicals America, Inc.	TPV	Milastomer™
Huafon EP158	Huafon Group Co., Ltd.	Nylon 66	Huafon
Innova R 870E	Innova SA	PS (HIPS)	Innova
LEXAN™ VR1820 resin	SABIC Innovative Plastics Europe	PC	LEXAN™
Hostacom HYP 376D 201104	LyondellBasell Industries	PP Homopolymer	Hostacom