TECACOMP® PPA TRM X black 3990
| Category: | PPA , Polyphthalamide |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PoODcr_TECACOMPPPATRMXblack3990.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Main features
Target Industries
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | |
| Apparent Density | 0.71 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (340°C/2.16 kg) | 50 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (340°C/2.16 kg) | 75.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Transverse flow | 1.2 | % | ISO 294-4 |
| Flow | 0.98 | % | ISO 294-4 |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 7500 | MPa | ISO 527-2/50 |
| Tensile Stress | 120 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.0 | % | ISO 527-2/50 |
| Flexural Modulus | 6700 | MPa | ISO 178 |
| Flexural Stress | 170 | MPa | ISO 178 |
| Compressive Modulus | 6000 | MPa | ISO 604 |
| Compressive Stress | 175 | MPa | ISO 604 |
| Flexural Strain | 3.5 | % | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Service Temperature | |||
| long term | 150 | °C | |
| short term | 250 | °C |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 40 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 270 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 140 | °C | ISO 75-2/A |
| Glass Transition Temperature | 100 - 140 | °C | DIN 53765 |
| Melting Temperature | 285 - 315 | °C | DIN 53765 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 80°C | 3.3E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 80°C | 6.7E-5 | cm/cm/°C | ISO 11359-2 |
| Thermal Conductivity | DIN EN 821 | ||
| -- 1 | 0.40 | W/m/K | DIN EN 821 |
| -- 2 | 0.50 | W/m/K | DIN EN 821 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 3.4E+13 | ohms | DIN EN 61340 |
| Volume Resistivity | 1.1E+16 | ohms·cm | DIN EN 61340 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | HB | IEC 60695-11-10, -20 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 120 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Processing (Melt) Temp | 315 - 340 | °C | |
| Mold Temperature | 100 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Through-plane |
| 2 . | In-plane |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sanren M3700C (Premium-grade) | SINOPEC Shanghai Petrochemical Co. Ltd. | PP Homopolymer | Sanren |
| SLOVALEN® PH 49 GF 40 | Plastcom | PP, Unspecified | SLOVALEN® |
| Mowiol® 4-98 | Kuraray Co., Ltd. | PVOH | Mowiol® |
| Next Nylon 66 Prime Series PG33-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| Plenco 02369 (Compression) | Plastics Engineering Co. | Phenolic | Plenco |