Hytrel® 6356
| Category: | TPC-ET , THERMOPLASTIC POLYESTER ELASTOMER |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Hytrel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PnReyx_Hytrel-6356.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 63 Shore D High Performance Polyester Elastomer |
| General Information | |
|---|---|
| Additive |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 9.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 8.50 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.5 | % | |
| Flow | 1.5 | % | |
| Water Absorption | |||
| 24 hr | 0.50 | % | ASTM D570 |
| 23°C, 24 hr, 2.00 mm | 0.60 | % | ISO 62 |
| Equilibrium, 23°C, 2.00 mm, 50% RH | 0.20 | % | ISO 62 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 63 | ||
| Shore D, 15 sec | 57 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 280 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 19.0 | MPa | |
| Break | 43.0 | MPa | |
| 5.0% Strain | 12.0 | MPa | |
| 10% Strain | 15.0 | MPa | |
| 50% Strain | 18.8 | MPa | |
| 100% Strain | 19.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 33 | % | |
| Break | > 300 | % | |
| Nominal Tensile Strain at Break | 500 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | ||
| 1 hr | 248 | MPa | |
| 1000 hr | 182 | MPa | |
| Flexural Modulus | 290 | MPa | ISO 178 |
| Abrasion Resistance | 110 | mm³ | ISO 4649 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Heat Capacity of Melt | 2150 | J/kg/°C | |
| Thermal Conductivity of Melt | 0.15 | W/m/K |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Effective Thermal Diffusivity | 0.0544 | cSt | |
| Emission of Organic Compounds | 2.50 | µgC/g | VDA 277 |
| Odor | 2.5 | VDA 270 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | ISO 34-1 | ||
| Across Flow | 150 | kN/m | |
| Flow | 160 | kN/m |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -40°C | 15 | kJ/m² | |
| -30°C | 25 | kJ/m² | |
| 23°C, Partial Break | 120 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 19 | kJ/m² | |
| 23°C | 81 | kJ/m² | |
| Tensile Impact Strength (23°C) | 300 | kJ/m² | ISO 8256/1 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 45.0 | °C | ISO 75-2/A |
| Brittleness Temperature | -96.0 | °C | ISO 974 |
| Glass Transition Temperature 1 | 0.00 | °C | ISO 11357-2 |
| Vicat Softening Temperature | |||
| -- | 195 | °C | ISO 306/A50 |
| -- | 100 | °C | ISO 306/B50 |
| Melting Temperature 2 | 210 | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | ||
| Flow | 1.8E-4 | cm/cm/°C | |
| Flow : -40 to 23°C | 1.5E-4 | cm/cm/°C | |
| Transverse | 1.8E-4 | cm/cm/°C | |
| Transverse : -40 to 23°C | 1.5E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 8.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 20 | kV/mm | IEC 60243-1 |
| Relative Permittivity | IEC 60250 | ||
| 100 Hz | 4.60 | ||
| 1 MHz | 4.10 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 0.012 | ||
| 1 MHz | 0.036 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Oxygen Index | 21 | % | ISO 4589-2 |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Density | 1.06 | g/cm³ |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 8200-65 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Titalon® 1100ST | Titan Plastics Compounds Co., Ltd. | Nylon 6 | Titalon® |
| Geon™ Vinyl Wire & Cable W1800L | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Wire & Cable |
| Hostaform® XT 90 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| POLYCHIM C 10 BB | POLYCHIM INDUSTRIES | PP Homopolymer | POLYCHIM |