PULSE™ XT9215

Category:	PC+ABS , PC/ABS Engineering Resin
Manufacturer:	Trinseo
Trademark:	PULSE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PnPcyw_PULSEXT9215.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

PULSE 9215 is an easy flow, high-heat, low density mineral filled PC/ABS resin delivering optimized performance for automotive exterior component applications requiring low CLTE for a better dimensional stability.

Benefits

Very low CLTE for an improved dimensional stability (smaller gaps) and a better fit and finish for optimal quality

High ductility and easy flow for more design freedom (larger/longer parts, optimized wall thickness)and better economics (improved cycle time)

Significant density advantage (up to 10% compared to a PC/PET) for lighter parts and optimized costs

Faster cycle times for a better process cost control

High gloss for painted applications with enhanced paint adhesion

Applications

Spoilers

Exterior trims

Roof bows

Roof rails

General Information
Features	Low density Highlight Sprayable Fast molding cycle High liquidity Heat resistance, medium
Uses	Application in Automobile Field Automotive exterior parts Car exterior decoration
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.25	g/cm³	ISO 1183/B
Apparent Density	0.63	g/cm³	ISO 60
Melt Mass-Flow Rate (MFR) (260°C/5.0 kg)	22	g/10 min	ISO 1133
Spiral Flow	44.0	cm
Molding Shrinkage	0.30 - 0.60	%	ISO 294-4
VOC Content	15.0	µg/g	VDA 277

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus ¹	4600	MPa	ISO 527-2
Tensile Stress (Yield)	58.0	MPa	ISO 527-2/50
Tensile Strain (Break)	20	%	ISO 527-2/50

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	8.0	kJ/m²	ISO 179/1eA
23°C	20	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature (1.8 MPa, Unannealed)	108	°C	ISO 75-2/A
Vicat Softening Temperature	134	°C	ISO 306/B50
CLTE - Flow (-30 to 80°C)	3.5E-5	cm/cm/°C	ISO 11359-2

Injection	Nominal Value	Unit
Drying Temperature	120	°C
Drying Time	5.5	hr
Processing (Melt) Temp	255 - 280	°C
Mold Temperature	60 - 80	°C

Note Message
1 .	1 mm/min

Resin Grade	Manufacturer	Category	Trademark
SOLLAMID B 2700 FV 50	Krisoll Resinas Plásticas Ltda.	Nylon 6	SOLLAMID
Stylac™ IM30	Asahi Kasei Chemicals Corporation	ABS	Stylac™
CP PRYME® Polypropylene PPH100-30M	Chase Plastics Services Inc.	PP Homopolymer	CP PRYME® Polypropylene
Sumiliteresin® PR-NVK 83 I	SBHPP	Phenolic	Sumiliteresin®
DAI-EL™ G-752	DAIKIN AMERICA, INC.	Fluorelastomer	DAI-EL™