SEETEC LLDPE UL312
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Corporation |
| Trademark: | SEETEC LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PmRlE5_SEETEC-LLDPE-UL312.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
UL312 is manufactured by Unipol process technology. UL312 has good mechanical properties, gel free and good processability. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.920 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.1 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 41.2 | MPa | |
| TD : Break, 40 µm, Blown Film | 37.3 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 740 | % | |
| TD : Break, 40 µm, Blown Film | 760 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 170 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 40.0 µm | 58.8 | kN/m | |
| TD : 40.0 µm | 107.9 | kN/m |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 73 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 11 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VICOTE® F809 Natural | Victrex plc | PEEK | VICOTE® |
| Andur 8-3 APLF | Anderson Development Company | PUR-Ester/TDI | Andur |
| ELIX™ ABS H802 | ELIX Polymers, S. L. | ABS | ELIX™ ABS |
| Karina CLEAR PVC COMPOUND 90/211-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Petrothene® Select GS707 | LyondellBasell Industries | LLDPE | Petrothene® Select |