LEXAN™ XHT2146 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PleLHy_LEXANXHT2146resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XHT2146 resin is a high flow, high heat polycarbonate copolymer with improved release performance compared to LEXAN XHT2141 resin. It is available in a range of opaque and limited transparent colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 46 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 43.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.23 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2600 | MPa | ASTM D638 |
| -- | 2600 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 70.0 | MPa | ASTM D638 |
| Yield | 70.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 60.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 6.5 | % | ASTM D638 |
| Yield | 6.5 | % | ISO 527-2/50 |
| Fracture 5 | 90 | % | ASTM D638 |
| Fracture | 90 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2550 | MPa | ASTM D790 |
| -- 7 | 2450 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 110 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C 9 | 9.0 | kJ/m² | ISO 179/1eA |
| 23°C 10 | 12 | kJ/m² | ISO 179/1eA |
| 23°C 11 | 20 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 12 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact | |||
| -30°C | 75 | J/m | ASTM D256 |
| 23°C | 120 | J/m | ASTM D256 |
| -30°C 13 | 9.0 | kJ/m² | ISO 180/1A |
| -30°C 14 | 10 | kJ/m² | ISO 180/1A |
| 23°C 15 | 10 | kJ/m² | ISO 180/1A |
| 23°C 16 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 17 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U | |
| Instrumented Dart Impact (23°C, Total Energy) | 68.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 155 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 18 | 155 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 145 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 19 | 142 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 161 | °C | ASTM D1525 20 |
| -- | 160 | °C | ISO 306/B50 |
| -- | 162 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Metallized Haze Onset | 155 | °C | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 125 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 270 - 300 | °C | |
| Middle Temperature | 280 - 320 | °C | |
| Front Temperature | 290 - 330 | °C | |
| Nozzle Temperature | 285 - 330 | °C | |
| Processing (Melt) Temp | 290 - 330 | °C | |
| Mold Temperature | 85.0 - 130 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 90 | rpm | |
| Vent Depth | 0.025 - 0.080 | mm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*3 sp=62mm |
| 10 . | 80*10*3 sp=62mm |
| 11 . | 80*10*4 sp=62mm |
| 12 . | 80*10*3 sp=62mm |
| 13 . | 80*10*3 |
| 14 . | 80*10*4 |
| 15 . | 80*10*3 |
| 16 . | 80*10*4 |
| 17 . | 80*10*3 |
| 18 . | 80*10*4 mm |
| 19 . | 80*10*4 mm |
| 20 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TEREZ PA 6.6 7750 T | TER HELL PLASTIC GMBH | Nylon 66 | TEREZ PA 6.6 |
| TPSiV™ 4200-60A | Multibase, A Dow Corning Company | TPSiV | TPSiV™ |
| Caltex PP RE72 | GS Caltex | TPO | Caltex PP |
| Axiall PVC 19853 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| Hanwha Total PP GB14 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |