Abstron SE22
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Bhansali Engineering Polymers Limited |
| Trademark: | Abstron |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PlT0Lh_Abstron-SE22.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Abstron SE22 is an Acrylonitrile Butadiene Styrene (ABS) product. It can be processed by pipe extrusion, profile extrusion, or sheet extrusion and is available in Asia Pacific. Applications of Abstron SE22 include plumbing/piping/potable water and sheet. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.09 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 10 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.60 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale, Injection Molded) | 110 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm, Injection Molded) | 44.1 | MPa | ASTM D638 |
| Flexural Modulus 2(6.40 mm, Injection Molded) | 2060 | MPa | ASTM D790 |
| Flexural Strength 3(6.40 mm, Injection Molded) | 61.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm, Injection Molded | 350 | J/m | |
| 23°C, 6.40 mm, Injection Molded | 290 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 4(1.8 MPa, Annealed, 6.40 mm, Injection Molded) | 94.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.20 mm) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Type I, 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | Annealed at 85°C for 2 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultralloy™ 50 | Hapco Inc. | TP, Unspecified | Ultralloy™ |
| ESTAPROP HK 4000 CH-HT | Cossa Polimeri S.r.l. | PP Copolymer | ESTAPROP |
| Fainplast PVC FKA 86/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| Ekalon® 8 E I | Sattler KunststoffWerk GmbH | PC | Ekalon® |
| Karina IVORY PVC COMPOUND 105915-35/1-B-IS-EC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |