PRE-ELEC® ESD 6300
| Category: | PS (HIPS) , High Impact Polystyrene |
| Manufacturer: | Premix Oy |
| Trademark: | PRE-ELEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PkaU4p_PRE-ELEC-ESD-6300.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRE-ELEC® ESD 6300 is a static dissipative thermoplastic compound based on high impact polystyrene. The dissipative property is permanent and built into the polymer chain. PRE-ELEC® ESD6300 has been developed for extrusion of thermoformable multilayer sheets and injection molding. Surface resistance values of 1e8 O (EOS/ESD S11.11-1993, IEC 61340-5-1) can be achieved with optimum processing parameters. The products made out of PRE-ELEC® ESD 6300 are washable, reusable, recyclable. PRE-ELEC® ESD 6300 is whitish in colour and can be coloured into various bright colours. Typical applications include injection moulded boxes, bins, thermoformed trays and clamshells when permanent ESD protection is required. These products can be used in electronics, medical, pharmaceutical and paper handling industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.08 | g/cm³ | ASTM D792 |
| -- | 1.07 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 11 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.50 - 0.70 | % | ASTM D955 |
| Flow direction | 0.50 - 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield | 15.9 | MPa | ASTM D638 |
| Yield | 16.0 | MPa | ISO 527-2 |
| -- | 13.8 | MPa | ASTM D638 |
| 4.00 mm | 14.0 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.0 | % | ASTM D638, ISO 527-2 |
| Fracture | 12 | % | ASTM D638 |
| Fracture, 4.00mm | 12 | % | ISO 527-2 |
| Flexural Modulus | |||
| 4.00 mm | 1240 | MPa | ASTM D790 |
| 4.00 mm | 1200 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 4.00 mm) | 4.20 | kJ/m² | ASTM D256 |
| Notched Izod Impact 1(23°C) | 4.0 | kJ/m² | ISO 180 |
| Unnotched Izod Impact (23°C, 4.00 mm) | 23.1 | kJ/m² | ASTM D256 |
| Unnotched Izod Impact Strength 2(23°C) | 24 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 81.1 | °C | ASTM D648B |
| 0.45 MPa, not annealed | 81.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 68.9 | °C | ASTM D648A |
| 1.8 MPa, not annealed | 69.0 | °C | ISO 75-2/Af |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | < 1.0E+9 | ohms | ESD STM11.11, IEC 61340-2-3 |
| Static Decay | |||
| -- | sec | ESD S20.20 | |
| -- | sec | IEC 61340-5-1 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Processing (Melt) Temp | 190 - 210 | °C | |
| Mold Temperature | 30.0 - 70.0 | °C | |
| Injection Pressure | 75.2 - 120 | MPa | |
| Injection Rate | Moderate |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 80.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 180 | °C | |
| Cylinder Zone 2 Temp. | 190 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Cylinder Zone 4 Temp. | 200 | °C | |
| Cylinder Zone 5 Temp. | 200 | °C |
| Extrusion instructions |
|---|
| Cylinder Zone 6: 200°C |
| Note Message | |
|---|---|
| 1 . | 4 mm thickness |
| 2 . | 4 mm thickness |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Provista™ Copolymer UVO | Eastman Chemical Company | Polyester, TP | Provista™ |
| Vinnolit® E 67 FF | Vinnolit GmbH & Co. KG | PVC, Unspecified | Vinnolit® |
| Westlake LDPE EC479AA | Westlake Chemical Corporation | LDPE | Westlake LDPE |
| PPR PPCO10 | Premier Plastic Resins, Inc. | PP Copolymer | PPR |
| Sylvin 8260-75 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |