Orgalloy® LE 60THM
| Category: | Nylon 6 Alloy , Polyamide 6 Alloy |
| Manufacturer: | Arkema |
| Trademark: | Orgalloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PkEGzZ_Orgalloy-LE-60THM.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Orgalloy® LE 60THM is a Polyamide 6 Alloy (Nylon 6 Alloy) product. It can be processed by blow molding, calendering, extrusion, film extrusion, injection molding, profile extrusion, resin transfer molding, sheet extrusion, or thermoforming and is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1050 | 1050 | kg/m³ | ISO 1183 1 |
| Melt volume-flow rate (235°C/2.16 kg) | 3.00 | -- | cm³/10min | ISO 1133 2 |
| Water Absorption | ISO 62 3 | |||
| Saturation | 6.0 | -- | % | |
| Equilibrium | 1.8 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile modulus | -- | 1750 | MPa | ISO 527-2 4 |
| Tensile Stress (Yield) | -- | 40.0 | MPa | ISO 527-2 5 |
| Tensile Strain (Yield) | -- | 5.0 | % | ISO 527-2 6 |
| Nominal strain at break | -- | > 50 | % | ISO 527-2 7 |
| Tensile Creep Modulus | ISO 899-1 8 | |||
| 1 hr | -- | 1520 | MPa | |
| 1000 hr | -- | 690 | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy notched impact strength | ISO 179/1eA 9 | |||
| -30°C | -- | 10.0 | kJ/m² | |
| 23°C | -- | 13.0 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ISO 75-2 10 | |||
| 0.45 MPa | 80.0 | -- | °C | |
| 1.8 MPa | 50.0 | -- | °C | |
| Melting Temperature 11 | 220 | -- | °C | ISO 11357-3 12 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface resistivity | -- | > 1.0E+15 | ohms | IEC 60093 13 |
| Comparative tracking index | -- | 600 | IEC 60112 14 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Behav. at 1.6mm nom. thickn. (1.60 mm) | HB | -- | ISO 1210 15 | |
| Burning Behav. at thickness h (3.20 mm) | HB | -- | ISO 1210 16 |
| Note Message | |
|---|---|
| 1 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 2 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 3 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 4 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 5 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 6 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 7 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 8 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 9 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 10 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 11 . | 10 °C/min |
| 12 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 13 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 14 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 15 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| 16 . | Tested in accordance with ISO 10350. 23°C/50%r.h. unless otherwise noted. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLPLAST TH 9000C | UTEKSOL d.o.o. | SBS | SOLPLAST TH |
| THERMOLAST® K TC7HBA (Series: AD/POM) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Adflex X 100 G | LyondellBasell Industries | TPO (POE) | Adflex |
| INEOS LDPE 19N430B | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| LITEN RL 58 UV | UNIPETROL RPA | LPE Copolymer | LITEN |