Spartech Polycom SCR7-7006UA
| Category: | PC , Polycarbonate |
| Manufacturer: | Spartech Polycom |
| Trademark: | Spartech |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PikBhZ_Spartech-Polycom-SCR7-7006UA.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Spartech SCR7-7006UA is a high viscosity PC resin for extrusion that features a UV stabilizer. It is suitable for outdoor use with respect to exposure to ultraviolet light, water exposure and immersion in accordance with UL746C. It is heat stabilized and lubricated for good processing characteristics. Polycarbonate resins span a wide range of physical properties that combine to make it one of the toughest, most versatile of all engineering thermoplastics. It is well known for its exceptional impact resistance, plus it has outstanding mechanical, electrical, and optical properties. A very versatile product for a wide variety of applications, Spartech SCR7-7006UA is recommended for industrial, transportation, sporting goods and electrical/electronic applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.3 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus (23°C) | 2140 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 94.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 850 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.52 mm, NC) | V-2 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 271 - 282 | °C | |
| Front Temperature | 282 - 299 | °C | |
| Nozzle Temperature | 277 - 304 | °C | |
| Processing (Melt) Temp | 288 - 316 | °C | |
| Mold Temperature | 71.1 - 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecopet® PT74 CR30 BK111 PR | Eurotec Engineering Plastics | PET | Tecopet® |
| ECOGRAN® PA66 | Eurocompound Polymers | Nylon 66 | ECOGRAN® |
| INEOS Wire & Cable BPD8128 | INEOS Olefins & Polymers Europe | LDPE | INEOS Wire & Cable |
| Karina IVORY PVC COMPOUND -E 600D35/ 1-C | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Polifil® Nylon 71MR | The Plastics Group | Nylon 66 | Polifil® Nylon |