OXPEKK® IG240C
| Category: | PEKK , Polyetherketoneketone |
| Manufacturer: | Oxford Performance Materials, Inc. |
| Trademark: | OXPEKK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PigZkP_OXPEKK-IG240C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
OXPEKK® IG240C is a Polyetherketoneketone (PEKK) material filled with 40% carbon fiber. It is available in Europe or North America. Typical application of OXPEKK® IG240C: Medical/Healthcare |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Uses |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.47 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.050 | % | ASTM D955 |
| Water Absorption (24 hr) | < 0.030 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3500 | MPa | ASTM D638 |
| Tensile Strength (Break) | 269 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.0 | % | ASTM D638 |
| Flexural Modulus | 3000 | MPa | ASTM D790 |
| Flexural Strength | 300 | MPa | ASTM D790 |
| Compressive Strength | 241 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 96 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 327 | °C | ASTM D648 |
| Glass Transition Temperature | 163 | °C | DSC |
| Melting Temperature | 360 | °C | DSC |
| CLTE - Flow | 1.1E-5 | cm/cm/°C | ASTM D696 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 86019-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Viton® A-201C | DuPont Performance Elastomers | Fluorelastomer | Viton® |
| LNP™ LUBRICOMP™ RFL26S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |
| LUVOCOM® 1106-8374 | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| CYCOLOY™ XCY620S resin | SABIC Innovative Plastics | PC+ABS | CYCOLOY™ |