VITAMIDE® BX30WT6173
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PiDXuU_VITAMIDE-BX30WT6173.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® BX30WT6173 is a Polyamide 6 (Nylon 6) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.38 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 1.5 | % | |
| Water Absorption (23°C, 24 hr) | 0.90 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 60.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 10 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2750 to 3000 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Break | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 15 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 200 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 220 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 3.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Dielectric Strength | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| Comparative Tracking Index | |||
| Solution A | 550 | V | IEC 60112 |
| -- 1 | 550 | V | ASTM D3638 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | V-0 | UL 94 | |
| Oxygen Index | 30 | % | ASTM D2863, ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | Solution A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene FRG220-773UV | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Moplen RP225N | LyondellBasell Industries | PP Random Copolymer | Moplen |
| CP PRYME® Nylon 66 NN233HSL BK | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Lionpol IM-36058 | Lion Polymers Incorporated | TPE | Lionpol |
| Rotuba CAB B9004 (22% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |