INSULCAST® RTVS 61M
| Category: | Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2 |
| Manufacturer: | ITW Polymers Coatings North America |
| Trademark: | INSULCAST® RTVS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PgoubT_INSULCAST-RTVS-61M.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| RTVS 61M is a low viscosity, self-extinguishing transparent RTVS Silicone. RTVS 61M is used in situations where component identification and protection against shock and vibration is needed. Heat can be used to accelerate the cure. |
| General Information | |
|---|---|
| Features |
|
| Hardness | Nominal Value | Test Method | |
|---|---|---|---|
| Durometer Hardness (Shore A) | 35 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 2.76 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 150 | % | ASTM D412 |
| Tear Strength 1 | 4.38 | kN/m | ASTM D624 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| CLTE - Flow | 2.7E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.19 | W/m/K | |
| Service Temperature | -55 to 204 | °C |
| Cured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Linear Shrinkage | 0.20 | % |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Dielectric Constant (1 kHz) | 2.70 | ASTM D150 | |
| Dissipation Factor (1 kHz) | 1.0E-3 | ASTM D150 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (25°C) | 26 | wk |
| Uncured Properties | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Color | |||
| -- 2 | Clear/Transparent | ||
| -- 3 | Clear/Transparent | ||
| Density | |||
| -- 4 | 0.998 | g/cm³ | |
| -- 5 | 0.998 | g/cm³ | |
| -- 6 | 1.02 | g/cm³ | |
| Viscosity | ASTM D2393 | ||
| -- 7 | 4.0 | Pa·s | |
| -- 8 | 4.5 | Pa·s | |
| -- 9 | 5.0 | Pa·s | |
| Curing Time | |||
| 95°C | 1.0 | hr | |
| 50°C | 2.0 | hr | |
| 25°C | 24 | hr | |
| Pot Life (25°C) | 120 | min |
| Note Message | |
|---|---|
| 1 . | Die B |
| 2 . | Part B |
| 3 . | Part A |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | Mixed |
| 7 . | Part A |
| 8 . | Mixed |
| 9 . | Part B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 301 GB 20 | RTP Company | PC | RTP |
| Spartech Polycom SCR1F-4080 | Spartech Polycom | ABS | Spartech |
| Celanex® 3200-2 | Celanese Corporation | PBT | Celanex® |
| DIC.PPS FZ-3500 | DIC Corporation | PPS | DIC.PPS |
| Sylvin 2900-75 Clear 8388 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |