Polymer-E F8101
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Asia Polymer Corporation (APC) |
| Trademark: | Polymer-E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PfmA1E_Polymer-E-F8101.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polymer-E F8101 is a Low Density Polyethylene product. It is available in Asia Pacific. Typical application: Film. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.923 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 51 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | < 0.060 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 32 µm, Blown Film | 186 | MPa | |
| 1% Secant, TD : 32 µm, Blown Film | 216 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 17.7 | MPa | |
| TD : Break, 32 µm, Blown Film | 13.7 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 32 µm, Blown Film | 400 | % | |
| TD : Break, 32 µm, Blown Film | 520 | % | |
| Dart Drop Impact (32 µm, Blown Film) | 50 | g | ASTM D1709 |
| Elmendorf Tear Strength 1 | ASTM D1922 | ||
| MD : 31.8 µm | 137.3 | kN/m | |
| TD : 31.8 µm | 78.5 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed) | 50.0 | °C | ASTM D648 |
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss (60°, 31.8 µm, Blown Film) | 105 | ASTM D523 | |
| Haze (31.8 µm, Blown Film) | 8.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TYRIN™ 7000 | The Dow Chemical Company | CPE | TYRIN™ |
| Exxtral™ Performance Polyolefin HMU216 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| ELASTOSIL® M 4500 | Wacker Chemie AG | Silicone | ELASTOSIL® M |
| GLS PP YN06 HF | GLS Polymers Pvt. Ltd. | PP, Unspecified | GLS PP |
| UBE Nylon 1015GC6 | UBE Engineering Plastics, S.A. | Nylon 6 | UBE Nylon |