LNP™ STAT-KON™ DE003P compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PeTuQR_LNP-STAT-KON-DE003P-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* DE003P is a compound based on Polycarbonate resin containing 15% Carbon Fiber. Added features of this material include: Electrically Conductive, Exceptional Processing. Also known as: LNP* STAT-KON* Compound DC-1003 EP Product reorder name: DE003P |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.040 to 0.10 | % | ASTM D955 |
| Across Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.32 to 0.41 | % | ISO 294-4 |
| Flow : 24 hr | 0.040 to 0.13 | % | ISO 294-4 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.15 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.40 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 11200 | MPa | ASTM D638 |
| -- | 9880 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 121 | MPa | ASTM D638 |
| Break | 110 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 1.8 | % | ASTM D638 |
| Break | 1.4 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 9930 | MPa | ASTM D790 |
| -- | 9770 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 193 | MPa | ASTM D790 |
| -- | 184 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 77 | J/m | ASTM D256 |
| 23°C 2 | 7.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 430 | J/m | ASTM D4812 |
| 23°C 3 | 33 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 16.2 | J | ASTM D3763 |
| -- | 3.85 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 145 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 4 | 146 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 143 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 5 | 143 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 2.2E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 1.3E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 4.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiprene® 3075 | Resirene, S.A. de C.V. | TPE | Resiprene® |
| Sylvin 8225-95 Natural | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| T-Blend® 5503N-PE | TSRC Corporation | TPE | T-Blend® |
| ACCUTECH™ HP0339W20L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Starex VH-0800 E | LOTTE ADVANCED MATERIALS CO., LTD. | ABS | Starex |