INNOPOL® PP CS 2-4630 FR
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Inno-Comp Ltd. |
| Trademark: | INNOPOL® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PdwdVo_INNOPOL-PP-CS-2-4630-FR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
INNOPOL® CS 2-4630 FR is a flame retarded polypropylene block-copolymer compound. This grade is available in nature and custom coloured form. INNOPOL® CS 2-4630 FR is recommended for producing injection moulded products, where the required properties are excellent flame retardancy (V0) besides balanced physical properties. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.950 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1300 | MPa | ISO 527-2/2 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 5.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 1450 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 3.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.0 | kJ/m² | ISO 179/1eA |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 90.0 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | FMVSS 302 | |
| Combustibility- Automotive materials (thickness d>1mm) | + | FMVSS 302 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Rear Temperature | 190 - 250 | °C | |
| Middle Temperature | 190 - 250 | °C | |
| Front Temperature | 190 - 250 | °C | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 10.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Hold pressure: 50 to 100 % of actual injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOTAL Polypropylene PPC 5720WZ | TOTAL Refining & Chemicals | PP Impact Copolymer | TOTAL Polypropylene |
| UMG ABS® EX10U | UMG ABS, Ltd. | ABS | UMG ABS® |
| AIE PC 10G6F | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Beetle® PBTS100 | Teknor Apex Company (Chem Polymer) | PBT | Beetle® |
| E-RIALFILL B 15 40 C | RIALTI Srl | PP, Unspecified | E-RIALFILL |