NORYL™ LS6010 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PdDFzP_NORYLLS6010resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| NORYL LS6010 resin is a high performance modified PPE-PS blend that exhibits an excellent balance of nonhalogenated flame retardance, lower smoke production upon burning and low specifc gravity for light weight parts. NORYL LS6010 is available in custom colors and may be an excellent material candidate for applications requiring light weight parts and strong flame, smoke and toxicity performance. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.11 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 5.7 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 5.70 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.80 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.20 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.050 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2220 | MPa | ASTM D638 |
| -- | 2440 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 64.0 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 53.0 | MPa | ASTM D638 |
| Fracture | 58.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 4.6 | % | ASTM D638 |
| Yield | 4.7 | % | ISO 527-2/50 |
| Fracture 5 | 20 | % | ASTM D638 |
| Fracture | 8.3 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2390 | MPa | ASTM D790 |
| -- 7 | 2360 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 100 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 100 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 20 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C | 180 | J/m | ASTM D256 |
| 23°C | 300 | J/m | ASTM D256 |
| -30°C 10 | 15 | kJ/m² | ISO 180/1A |
| 23°C 11 | 19 | kJ/m² | ISO 180/1A |
| Instrumented Dart Impact (23°C, Total Energy) | 52.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, unannealed, 3.20mm | 122 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 12 | 124 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 143 | °C | ASTM D1525, ISO 306/B50 10 13 |
| -- | 146 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 6.7E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Draeger Tube Toxicity | ASTM E662 | ||
| Flaming : 1.52 mm | Pass | ASTM E662 | |
| Non-Flaming : 1.52 mm | Pass | ASTM E662 | |
| Flame Spread Index (1.52 mm) | 15.0 | ASTM E162 | |
| NBS Smoke Density | ASTM E662 | ||
| Flaming, 4 min : 1.52 mm | 30.0 | ASTM E662 | |
| Non-Flaming, 4 min : 1.52 mm | 7.00 | ASTM E662 | |
| Vertical Burn Test | FAR 25.853 | ||
| Test a (60 s, 1.52 mm), passes at | 0.0 | hr | FAR 25.853 |
| Test b (12 s, 1.52 mm), passes at | 4.00 | sec | FAR 25.853 |
| Extrusion instructions |
|---|
| Profile Extrusion Parameters: Adapter Temperature: 220 - 260 °C Barrel - Zone 1 Temperature: 220 - 260 °C Barrel - Zone 2 Temperature: 220 - 260 °C Barrel - Zone 3 Temperature: 220 - 260 °C Barrel - Zone 4 Temperature: 220 - 260 °C Calibrator Temperature: 30 - 60 °C Die Temperature: 220 - 260 °C Drying Temperature: 95 - 105 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 12 hrs Hopper Temperature: 80 - 120 °C Maximum Moisture Content: 0.07 % Melt Temperature: 220 - 260 °C Water Bath Temperature: 30 - 50 °C Sheet Extrusion Parameters: Adapter Temperature: 220 - 260 °C Barrel - Zone 1 Temperature: 220 - 260 °C Barrel - Zone 2 Temperature: 220 - 260 °C Barrel - Zone 3 Temperature: 220 - 260 °C Barrel - Zone 4 Temperature: 220 - 260 °C Die Temperature: 220 - 260 °C Drying Temperature: 95 - 105 °C Drying Time: 2 - 4 hrs Drying Time (Cumulative): 12 hrs Maximum Moisture Content: 0.07 % Melt Temperature: 220 - 260 °C Roll Stack Temp - Bottom: 90 - 150 °C Roll Stack Temp - Middle: 90 - 150 °C Roll Stack Temp - Top: 90 - 150 °C |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 sp=62mm |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 |
| 12 . | 80*10*4 mm |
| 13 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1687 | RTP Company | PAS | RTP |
| Styrolution PS 6200/6201 | INEOS Styrolution Group GmbH | PS (HIPS) | Styrolution PS |
| Flontech® FT-GR10-6 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Grilamid® XE 4108 black 9992 | EMS-GRIVORY | Nylon 6/12 | Grilamid® |
| SIBUR Synthetic Rubber NBR 2645 | SIBUR | NBR | SIBUR Synthetic Rubber |