Dryflex® A2 602601

Category:	SEBS , Styrene Ethylene Butylene Styrene Block Copolymer
Manufacturer:	ELASTO
Trademark:	Dryflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PdCVLP_Dryflex-A2-602601.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
Dryflex A thermoplastic elastomer (TPE) bondable grades, primarily based on SBS and SEBS, increase freedom of design and open up a vast range of application opportunities. It used to be a complex and costly affair producing details made of thermoplastics that showed soft-touch qualities or had integrated seals. With Dryflex A TPEs, since the materials are bonded together at the production stage, no separate primer or adhesive is needed. This makes the process faster and more cost-effective than if the two parts were assembled together after each had been produced separately, or bonded mechanically, which often requires some modification to the design. Primarily a TPE is used as the soft component. Dryflex A bondable grades can be co-extruded or overmoulded with a variety of engineering plastics. Dryflex A grades are available in black or natural and can easily be coloured. These thermoplastic elastomers form excellent bonds onto PP, PE, PA, ABS, PC, PS, PMMA, ASA, SAN and their blends. Polyamides and ABS may be either reinforced or non-reinforced yet still bond extremely well to Dryflex. It is easy to achieve excellent bonding to PP, even using standard TPE materials, while other thermoplastics require some modification of the TPE material to optimise bonding.

Message

Dryflex A thermoplastic elastomer (TPE) bondable grades, primarily based on SBS and SEBS, increase freedom of design and open up a vast range of application opportunities.

It used to be a complex and costly affair producing details made of thermoplastics that showed soft-touch qualities or had integrated seals. With Dryflex A TPEs, since the materials are bonded together at the production stage, no separate primer or adhesive is needed. This makes the process faster and more cost-effective than if the two parts were assembled together after each had been produced separately, or bonded mechanically, which often requires some modification to the design.

Primarily a TPE is used as the soft component. Dryflex A bondable grades can be co-extruded or overmoulded with a variety of engineering plastics.

Dryflex A grades are available in black or natural and can easily be coloured. These thermoplastic elastomers form excellent bonds onto PP, PE, PA, ABS, PC, PS, PMMA, ASA, SAN and their blends. Polyamides and ABS may be either reinforced or non-reinforced yet still bond extremely well to Dryflex. It is easy to achieve excellent bonding to PP, even using standard TPE materials, while other thermoplastics require some modification of the TPE material to optimise bonding.

General Information
Features	Bondability Good Adhesion Good Chemical Resistance Good UV Resistance
Appearance	Black
Forms	Pellets
Processing Method	Extrusion Injection Molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.19	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 4.00 mm)	60		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength			ASTM D638
--	4.60	MPa
100% Strain	2.20	MPa
300% Strain	3.40	MPa
Tensile Elongation (Break)	550	%	ASTM D638

Elastomers	Nominal Value	Unit	Test Method
Tear Strength	26.0	kN/m	ASTM D624

Thermal	Nominal Value	Unit
Service Temperature	-50 to 125	°C

Additional Information	Nominal Value		Test Method
Peel Force ¹	Cohesive		ASTM D903

Note Message
1 .	Tests conducted on overmoulded test specimens, 2.5mm thick with a 90° peel angle

Resin Grade	Manufacturer	Category	Trademark
SABIC® HDPE P5510NT	SABIC Americas, Inc.	HDPE	SABIC® HDPE
SEPAZ™ C400HD	Mando Advanced Materials Co., Ltd.	LCP	SEPAZ™
Evermore PUR SW-8021HR	Evermore Chemical Industry Co., Ltd.	PUR, Unspecified	Evermore PUR
DynaMix™ XP-5531	Polymer Dynamix	TP, Unspecified	DynaMix™
LNP™ LUBRICOMP™ ZX05506 compound	SABIC Innovative Plastics	PPE+PS	LNP™ LUBRICOMP™