Lupoy® EF5001RFT
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PbleZo_Lupoy-EF5001RFT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy®EF5001RFT is a polycarbonate acrylonitrile butadiene styrene (PC ABS) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Lupoy®The main features of the EF5001RFT are:
Lupoy®The typical application fields of EF5001RFT are: housing |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.19 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 - 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 56.9 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 30 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2450 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 3.20 mm) | 93.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (0.45 MPa, Unannealed, 6.40 mm) | 94.0 | °C | ASTM D648 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Rear Temperature | 220 - 240 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 230 - 250 | °C | |
| Nozzle Temperature | 230 - 250 | °C | |
| Processing (Melt) Temp | 240 - 260 | °C | |
| Mold Temperature | 60.0 - 80.0 | °C | |
| Back Pressure | 0.981 - 3.92 | MPa | |
| Screw Speed | 40 - 70 | rpm |
| Extrusion instructions |
|---|
| Minimum Moisture Content: 0.04% |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecolen® HP30 KG30 NL HS 0B | Eurotec Engineering Plastics | PP Homopolymer | Tecolen® |
| Anjacom® 465-GF15 | Almaak International GmbH | PBT+ASA | Anjacom® |
| Estane® R195A-9 TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Fluon® LM-ETFE AH-3000 | Asahi Glass Co., Ltd. | ETFE | Fluon® |
| KRALASTIC® ST-200 | Nippon A&L Inc. | ABS | KRALASTIC® |