SCHULAMID® 66 GF 35 FC4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PZrLrS_SCHULAMID-66-GF-35-FC4.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, 35% glassfiber reinforced with KTW approval til 85°C |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183/A |
| Viscosity Number | 145 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 10500 | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 195 | 130 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 2.8 | 3.0 | % | ISO 527-2/1A/5 |
| Flexural Modulus 1 | 9000 | -- | MPa | ISO 178 |
| Flexural Stress 2(3.7% Strain) | 265 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | -- | kJ/m² | |
| 23°C | 11 | 17 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 80 | -- | kJ/m² | |
| 23°C | 83 | 85 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 250 | -- | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 250 | -- | °C | ISO 75-2/Af |
| Vicat Softening Temperature | 250 | -- | °C | ISO 306/B50 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TOYOBO Urethane E1080A | TOYOBO America, Inc. | PUR-Butyl | TOYOBO Urethane |
| Nipolon® -Z Nipolon®-Z | TOSOH Corporation | LLDPE | Nipolon® -Z |
| Electrafil® J-50/CF/10 | Techmer Engineered Solutions | PC | Electrafil® |
| Elvacite® 2013 | Lucite International Inc. | Acrylic (PMMA) | Elvacite® |
| Karina IVORY PVC COMPOUND -E ML-IS-FLEX-PO (*) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |