NatureFlex™ NE30 (42µ)
| Category: | Cellulose, Regenerated , Regenerated Cellulose |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | NatureFlex™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PZ9hdA_NatureFlex-NE30-42-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NatureFlex™ NE30 (42µ) is a Regenerated Cellulose product. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. Typical application: Film. Characteristics include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction 1(vs. Itself - Dynamic) | 0.30 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 41 µm | > 3000 | MPa | |
| 1% Secant, TD : 41 µm | > 1500 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 41 µm | 125 | MPa | |
| TD : Yield, 41 µm | 70.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 41 µm | 22 | % | |
| TD : Break, 41 µm | 70 | % | |
| Seal Strength 2 | 0.16 | N/mm | Internal Method |
| Seal Initiation Temperature (41 µm) | 80.0 to 200 | °C | Internal Method |
| Oxygen Transmission Rate (Wet) (23°C, 41 µm, 0.0% RH) | 3.00 | cm³/m²/24 hr | ASTM F1927 |
| Water Vapor Transmission | |||
| -- 3 | 15 | g/m²/24 hr | DIN 53122 |
| -- 4 | 15 | g/m²/24 hr | BS 3177 |
| -- 5 | 30 | g/m²/24 hr | ASTM E96 |
| Film Gauge | 41.3 | µm | Internal Method |
| Yield (413 mm) | 16.8 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 41.3 µm) | 90 | ASTM D2457 | |
| Haze 6(41.3 µm) | 6.0 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | Thickness: 41.3µ |
| 2 . | Thickness: 41.3µ |
| 3 . | 23°C, 85%RH, thickness: 41.3µ |
| 4 . | 25°C, 75%RH, thickness: 41.3µ |
| 5 . | 38°C, 90%RH, thickness: 41.3µ |
| 6 . | 2.5° wide angle |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| T-Blend® 4404N-SP | TSRC Corporation | TPE | T-Blend® |
| VESTORAN® 1900GF20 | Evonik Industries AG | PPE | VESTORAN® |
| Alcryn® 2170 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| EPO-TEK® H54 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| ARLEN™ AE2230 | Mitsui Chemicals America, Inc. | Nylon 6T | ARLEN™ |