LNP™ THERMOCOMP™ LF002 compound
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PZ6qbz_LNPTHERMOCOMPLF002compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| LNP THERMOCOMP LF002 is a compound based on Polyetheretherketone resin contaninig Glass Fiber. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 5700 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 97.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Yield) | 3.3 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 4700 | MPa | ISO 178 |
| Flexural Stress | 162 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 2(23°C) | 6.0 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 3(23°C) | 50 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 159 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 3.5E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 5.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 - 149 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Rear Temperature | 349 - 360 | °C | |
| Middle Temperature | 366 - 377 | °C | |
| Front Temperature | 382 - 393 | °C | |
| Processing (Melt) Temp | 382 - 388 | °C | |
| Mold Temperature | 138 - 166 | °C | |
| Back Pressure | 0.344 - 0.689 | MPa | |
| Screw Speed | 60 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxxam™ PP5140F D30 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| Sinvicomp SSZ6061 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| VITAMIDE® AR16RD6051 | Jackdaw Polymers | Nylon 66 | VITAMIDE® |
| Hifax TRC 221X 1 BLACK | LyondellBasell Industries | PP Copolymer | Hifax |
| Sylvin 3200-70 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |