Badamid® B70 TM-Z3
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PXCAax_Badamid-B70-TM-Z3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Chemical modified standard injection moulding grade, super tough |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.06 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 8.1 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.6 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 2100 | 1000 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 50.0 | 40.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 5.0 | 22 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 3(23°C) | > 50 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | No Break | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 6(1.8 MPa, Unannealed) | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 7 | 222 | -- | °C | ISO 3146 |
| CLTE - Flow 8(4.00 mm) | 8.4E-5 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 70 | -- | °C | |
| some hours | 160 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 9 | 1.0E+12 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 10 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 11 | 100 | 65 | kV/mm | IEC 60243-1 |
| Relative Permittivity 12(1 MHz) | 3.20 | 6.40 | IEC 60250 | |
| Dissipation Factor 13(1 MHz) | 0.012 | 0.10 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 14 | HB | -- | ||
| 1.60 mm 15 | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 110x10x4mm |
| 7 . | 10 K/min, Compounded for moulding |
| 8 . | >=10x10x4 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 125x13x0.8 mm |
| 15 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEFTEKHIM PP 4210L (EP2C30F) | Nizhnekamskneftekhim Inc. | PP Copolymer | NEFTEKHIM PP |
| Elastron® V V201.A87.B | Elastron USA, Inc. | TPV | Elastron® V |
| Karina BLACK PVC COMPOUND 601-48/ 1-BY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| PermaStat® 1000 | RTP Company | PBT | PermaStat® |
| Sylvin 8036-85 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |