TECACOMP® PA66 CF10 black 9084
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Ensinger GmbH |
| Trademark: | TECACOMP® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PWqAUI_TECACOMPPA66CF10black9084.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TECACOMP®PA66 CF10 black 9084 is a polyamide 66 (nylon 66) product that contains 10% carbon fiber reinforcement. It can be processed by injection molding and is available in Europe. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | |
| Apparent Density | 0.53 | g/cm³ | ISO 60 |
| Viscosity Number (H2SO4 (Sulphuric Acid)) | 210 | cm³/g | ISO 307 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8200 | MPa | ISO 527-2/50 |
| Tensile Stress | 155 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 3.3 | % | ISO 527-2/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 50 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | DIN 53765 | ||
| -- 1 | 5.00 | °C | DIN 53765 |
| -- 2 | 72.0 | °C | DIN 53765 |
| Melting Temperature | 160 | °C | DIN 53765 |
| Service Temperature | |||
| long term | 110 | °C | |
| short term | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 4.4E+12 | ohms | DIN EN 61340 |
| Volume Resistivity | 3.8E+13 | ohms·cm | DIN EN 61340 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 4.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | Moist |
| 2 . | Dry |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Teflon® FEP 9302 | DuPont Fluoropolymers | FEP | Teflon® FEP |
| Wondel® A AG5T | Nanjing Julong Engineering Plastics Co., LTD | Nylon 66 | Wondel® A |
| Emulprene® 1778R | INSA | SBR, Emulsion | Emulprene® |
| Piolen® P X7010 | PiO Kunststoffe GmbH & Co KG | PP Homopolymer | Piolen® P |
| LNP™ STAT-KON™ DD0001 compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |