AKROMID® B3 S1 natural (3715)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PVsA2U_AKROMID-B3-S1-natural-3715-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B3 S1 natural (3715) is an nonreinforced, cold impact strength polyamide 6 with light inherent color Applications are mountings and dowels in the furniture and construction industry |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.05 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 60.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 1.9 | -- | % | |
| Flow | 1.5 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.0 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2000 | 550 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 50.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | |||
| Yield | 4.2 | 30 | % | |
| Break | > 50 | > 100 | % | |
| Flexural Modulus 1 | 1500 | 650 | MPa | ISO 178 |
| Flexural Stress 2 | ISO 178 | |||
| -- 3 | 50.0 | -- | MPa | |
| -- | 65.0 | -- | MPa |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 55 | 45 | kJ/m² | |
| 23°C | 50 | 110 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 48.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 4 | 223 | -- | °C | DIN EN 11357-1 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 5(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | Standard Flexural Stress |
| 4 . | 10 K/min, DSC |
| 5 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ryton® R-4 | Solvay Specialty Polymers | PPS | Ryton® |
| Safron® H713-06 | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| SuperLite® SL550700-100 (2.0mm) | Azdel, Inc. | PP, Unspecified | SuperLite® |
| Nymax™ GF 1200 A 55 HS Natural | PolyOne Corporation | Nylon 66 | Nymax™ |
| ALCOM® PP 620/10 GY1464-04MCF | ALBIS PLASTIC GmbH | PP Homopolymer | ALCOM® PP |