HANWHA 3081
| Category: | HDPE , High Density Polyethylene |
| Manufacturer: | Hanwha Chemical |
| Trademark: | HANWHA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PVq4eW_HANWHA-3081.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
HANWHA HDPE 3081 is manufactured by Unipol process and designed for general purpose. HDPE 3081 has well balanced property of mechanical property and processability.
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.952 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.060 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 770 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 20 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 20 µm | 53.0 | MPa | ASTM D882 |
| TD : Break, 20 µm | 54.9 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 20 µm | 400 | % | ASTM D882 |
| TD : Break, 20 µm | 540 | % | ASTM D882 |
| Dart Drop Impact (20 µm) | 150 | g | ASTM D1709 |
| Tensile Tear Strength | ASTM D1004 | ||
| MD | 225.6 | kN/m | ASTM D1004 |
| TD | 181.4 | kN/m | ASTM D1004 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (20.0 µm) | 84 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio : 2 ~ 3Optimum Gage Range : 0.03 ~ 0.1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC V150-70 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| CGPC PVC SO-30X (30 phr Plasticizer A) | China General Plastics Corporation | PVC, Flexible | CGPC PVC |
| ASI POLYPROPYLENE PP 3503-01 | A. Schulman Inc. | PP Homopolymer | ASI POLYPROPYLENE |
| LNP™ STAT-KON™ DE0049P compound | SABIC Innovative Plastics | PC | LNP™ STAT-KON™ |
| LONOY lonoy 6100 | Kingfa | PC+PBT | LONOY |