LEXAN™ 4795R resin
| Category: | PPC , Polyphthalate Carbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PUpglZ_LEXAN4795Rresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LEXAN 4795R is a high heat resistant poly(ester)carbonate injection molding resin. Flame Retardant. |
| General Information | |
|---|---|
| Features |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 15 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2170 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 68.0 | MPa | ASTM D638 |
| Fracture | 70.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 7.5 | % | ASTM D638 |
| Fracture | 120 | % | ASTM D638 |
| Flexural Modulus 4(50.0 mm Span) | 2210 | MPa | ASTM D790 |
| Flexural Strength 5(Break, 50.0 mm Span) | 105 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 580 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 2100 | J/m | ASTM D4812 |
| Instrumented Dart Impact | ASTM D3763 | ||
| 23°C, Energy at Peak Load | 73.0 | J | ASTM D3763 |
| 23°C, Total Energy | 77.0 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 160 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 147 | °C | ASTM D648 |
| Vicat Softening Temperature | 164 | °C | ASTM D1525 6 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 327 - 349 | °C | |
| Middle Temperature | 338 - 360 | °C | |
| Front Temperature | 349 - 371 | °C | |
| Nozzle Temperature | 343 - 366 | °C | |
| Processing (Melt) Temp | 349 - 371 | °C | |
| Mold Temperature | 82.2 - 116 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 40 - 70 | rpm | |
| Vent Depth | 0.025 - 0.076 | mm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Niuk TPC1008 (General) | Shanghai Niuk New Plastic Technology Co., Ltd. | Acetal (POM) Copolymer | Niuk |
| ACRYLITE® Film 0F014 | Evonik Cyro LLC | Film, PMMA | ACRYLITE® Film |
| Alpha PVC GW 2326-A-VW1 NAT LCF | AlphaGary | PVC, Unspecified | Alpha PVC |
| apilon 52c® C S200 | API SpA | TPU-Polyester | apilon 52c® |
| LNP™ STAT-KON™ KE004 compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ STAT-KON™ |