Michimid K4100GF13-02
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | API Polymers, Inc. |
| Trademark: | Michimid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PTVBM9_Michimid-K4100GF13-02.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Michimid K4100GF13-02 is a Polyamide 6 (Nylon 6) product filled with 13% glass fiber. It is available in North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.22 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 93.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638 |
| Flexural Modulus - Tangent | 5000 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 191 | °C | |
| Melting Temperature | 215 | °C | ASTM D789 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 76.7 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 | °C | |
| Middle Temperature | 271 | °C | |
| Front Temperature | 271 | °C | |
| Nozzle Temperature | 266 | °C | |
| Processing (Melt) Temp | 277 | °C | |
| Mold Temperature | 79.4 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Pyramid™ II230 | Polymics, Ltd. | PEI | Pyramid™ |
| SCLAIR® 56B4 | NOVA Chemicals | HDPE | SCLAIR® |
| Glastic® SLC-1000 | Bulk Molding Compounds, Inc. | Polyester, TS | Glastic® |
| Hanwha Total PP BI530 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, High Crystal | Hanwha Total PP |
| Karina BEIGE PVC COMPOUND 801-08/ 98-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |