FluorLoop® CH10/1001
| Category: | PVDF , Polyvinylidene Fluoride |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | FluorLoop® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PTFdR1_FluorLoopCH101001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FluorLoop® CH10/1001 is typically processed by extrusion, mainly for film extrusion applications. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.75 - 1.80 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 4.0 - 8.0 | g/10 min | ASTM D1238 |
| Water Absorption (23°C, 24 hr) | < 0.040 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C, 2.00 mm) | 1700 - 2500 | MPa | ASTM D638 |
| Tensile Strength 2 | ASTM D638 | ||
| Yield, 23°C, 2.00mm | 50.0 - 60.0 | MPa | ASTM D638 |
| Fracture, 23°C, 2.00mm | 30.0 - 50.0 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield, 23°C, 2.00mm | 5.0 - 10 | % | ASTM D638 |
| Fracture, 23°C, 2.00mm | 20 - 300 | % | ASTM D638 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Peak Melting Temperature | 170 - 175 | °C | ASTM D3418 |
| Peak Crystallization Temperature (DSC) | 137 - 144 | °C | ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (23°C, 1.00 mm) | 20 - 25 | kV/mm | ASTM D149 |
| Dielectric Constant (23°C, 1 kHz) | 7.00 - 10.0 | ASTM D150 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.100 mm) | V-0 | UL 94 | |
| Oxygen Index (3.00 mm) | 44 | % | ASTM D2863 |
| Note Message | |
|---|---|
| 1 . | Type 4, 1.0mm/min |
| 2 . | Type 4, 50mm/min |
| 3 . | Type 4, 50mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong Aobang TPU-Polyester 90-A | Shandong Aobang Chemical Technology Co.,Ltd. | TPU-Polyester | Shandong Aobang TPU-Polyester |
| KRATON® D1116 E | Kraton Polymers LLC | SBS | KRATON® |
| LNP™ STAT-KON™ WEF42ISP compound | SABIC Innovative Plastics Europe | PBT | LNP™ STAT-KON™ |
| LNP™ THERMOCOMP™ KF002XXP compound | SABIC Innovative Plastics | Acetal (POM) Copolymer | LNP™ THERMOCOMP™ |
| NYLOY® MG-0813B | Nytex Composites Co., Ltd. | Nylon 66 | NYLOY® |