POCAN® T 7323 000000

Category:	PBT+PET , Polybutylene Terephthalate + PET
Manufacturer:	LANXESS GmbH
Trademark:	POCAN®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	PQCG7V_POCAN-T-7323-000000.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message
PBT+PET, 20 % glass fibers, injection molding, improved surface finish, increased temperature peak load

General Information
Filler / Reinforcement	Glass Fiber, 20% Filler by Weight
Features	Good Surface Finish Good UV Resistance Medium Heat Resistance
Processing Method	Injection Molding
Multi-Point Data	Creep Modulus vs. Time (ISO 11403-1) Isochronous Stress vs. Strain (ISO 11403-1) Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1) Shear Modulus vs. Temperature (ISO 11403-1) Viscosity vs. Shear Rate (ISO 11403-2)

Physical	Nominal Value	Unit	Test Method
Density (23°C)	1.47	g/cm³	ISO 1183
Apparent Density	0.80	g/cm³	ISO 60
Melt Volume-Flow Rate (MVR) (260°C/2.16 kg)	15.0	cm³/10min	ISO 1133
Molding Shrinkage			ISO 2577
Across Flow : 270°C, 2.00 mm ¹	1.0	%
Across Flow : 120°C, 4 hr, 2.00 mm ²	0.20	%
Flow : 270°C, 2.00 mm ³	0.40	%
Flow : 120°C, 4 hr, 2.00 mm ⁴	0.10	%
Water Absorption			ISO 62
Saturation, 23°C	0.40	%
Equilibrium, 23°C, 50% RH	0.20	%
Viscosity Number (Reduced Viscosity)	92.0	ml/g	ISO 1628

Hardness	Nominal Value	Unit	Test Method
Ball Indentation Hardness	175	MPa	ISO 2039-1

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus (23°C)	7500	MPa	ISO 527-2/1
Tensile Stress (Break, 23°C)	120	MPa	ISO 527-2/5
Tensile Strain (Break, 23°C)	3.2	%	ISO 527-2/5
Tensile Creep Modulus			ISO 899-1
1 hr	7200	MPa
1000 hr	6100	MPa
Flexural Modulus ⁵(23°C)	7500	MPa	ISO 178/A
Flexural Stress			ISO 178/A
3.5% Strain, 23°C	195	MPa
23°C ⁶	195	MPa
Flexural Strain at Flexural Strength (23°C) ⁷	3.5	%	ISO 178/A

Thermal	Nominal Value	Unit	Test Method
Halving Interval			IEC 60216
Electric Strength	10.2	°C
Tensile Impact Strength : 1.50 mm	13.5	°C
Tensile Strength : 1.50 mm	10.2	°C
Temperature Index			IEC 60216
Electric Strength, 20000 hr	150	°C
Tensile Impact Strength, 20000 hr : 1.50 mm	130	°C
Tensile Strength, 20000 hr : 1.50 mm	150	°C

Additional Information	Nominal Value		Test Method
Electrolytical Corrosion (23°C)	A 1		IEC 60426
ISO Shortname	PBT+PET, GHMR, 09-070, GF20		ISO 7792

Injection	Nominal Value	Unit	Test Method
Residual Moisture Content	0.0 to 0.020	%	Karl Fisher

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength			ISO 179/1eA
-30°C	< 10	kJ/m²
23°C	< 10	kJ/m²
Charpy Unnotched Impact Strength			ISO 179/1eU
-30°C	35	kJ/m²
23°C	40	kJ/m²
Notched Izod Impact Strength			ISO 180/1A
-40°C	< 10	kJ/m²
-30°C	< 10	kJ/m²
23°C	< 10	kJ/m²
Unnotched Izod Impact Strength			ISO 180/1U
-30°C	35	kJ/m²
23°C	35	kJ/m²

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, Unannealed	220	°C	ISO 75-2/B
1.8 MPa, Unannealed	195	°C	ISO 75-2/A
Vicat Softening Temperature	205	°C	ISO 306/B50
Ball Pressure Test (215°C)	Pass		IEC 60695-10-2
Melting Temperature ⁸	225 to 250	°C	ISO 11357-3
CLTE			ISO 11359-2
Flow : 23 to 55°C	3.0E-5	cm/cm/°C
Transverse : 23 to 55°C	9.0E-5	cm/cm/°C
Thermal Conductivity (23°C)	0.26	W/m/K	ISO 8302

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	> 1.0E+15	ohms	IEC 60093
Volume Resistivity (23°C)	> 1.0E+15	ohms·cm	IEC 60093
Electric Strength (23°C, 1.00 mm)	24	kV/mm	IEC 60243-1
Relative Permittivity			IEC 60250
23°C, 100 Hz	3.80
23°C, 1 MHz	3.60
Dissipation Factor			IEC 60250
23°C, 100 Hz	1.8E-3
23°C, 1 MHz	0.017
Comparative Tracking Index (Solution A)	250	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
0.800 mm	HB
1.60 mm	HB
Glow Wire Flammability Index (2.00 mm)	750	°C	IEC 60695-2-12
Oxygen Index ⁹	21	%	ISO 4589-2

Injection	Nominal Value	Unit	Test Method
Drying Temperature - Circulation Dryer	120	°C
Drying Time - Circulation Dryer	4.0 to 8.0	hr
Processing (Melt) Temp	260 to 280	°C
Mold Temperature	80.0 to 100	°C

Note Message
1 .	60x60x2mm, 90°C MT, 600 bar
2 .	60x60x2mm
3 .	60x60x2mm, 90°C MT, 600 bar
4 .	60x60x2mm
5 .	2.0 mm/min
6 .	2.0 mm/min
7 .	2 mm/min
8 .	10°C/min
9 .	Procedure A

Resin Grade	Manufacturer	Category	Trademark
RTP 1300 AR 15 TFE 15 SI 2	RTP Company	PPS	RTP
SABIC® LLDPE 6318BE	Saudi Basic Industries Corporation (SABIC)	LLDPE	SABIC® LLDPE
SCANAMID 6 B22^E F15	Polykemi AB	Nylon 6	SCANAMID 6
DILAMID® 6 FV 15 NATURAL	Dilaplast S.p.A.	Nylon 6	DILAMID®
LNP™ STAT-KON™ DEL22P compound	SABIC Innovative Plastics	PC	LNP™ STAT-KON™