LNP™ LUBRILOY™ RF206XXH compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRILOY™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | POU7L7_LNP-LUBRILOY-RF206XXH-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRILOY* RF206H is a compound based on Nylon 66 resin containing 30% Glass Fiber, Proprietary Lubricant. Added features of this material include: Wear Resistant, Healthcare Also known as: LNP* LUBRILOY* Compound RF-30 HC Product reorder name: RF206XXH |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.24 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.30 to 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 1.1 to 1.2 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.32 to 0.44 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.35 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8890 | MPa | ASTM D638 |
| -- | 8200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break | 122 | MPa | ASTM D638 |
| Break | 121 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Break | 2.6 | % | ASTM D638 |
| Break | 2.7 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 6830 | MPa | ASTM D790 |
| -- | 8500 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 179 | MPa | ASTM D790 |
| -- | 193 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.62 | ||
| vs. Itself - Static | 0.43 | ||
| Wear Factor - Washer | 29.0 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 120 | J/m | ASTM D256 |
| 23°C 2 | 12 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 760 | J/m | ASTM D4812 |
| 23°C 3 | 49 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 12.5 | J | ASTM D3763 |
| -- | 3.42 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 258 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 3.20 mm | 241 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 238 | °C | ISO 75-2/Af |
| CLTE | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 3.7E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 6.9E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 to 0.25 | % | |
| Rear Temperature | 266 to 277 | °C | |
| Middle Temperature | 282 to 293 | °C | |
| Front Temperature | 293 to 304 | °C | |
| Processing (Melt) Temp | 271 to 282 | °C | |
| Mold Temperature | 82.2 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MarFlex® 7105D | Chevron Phillips Chemical Company LLC | LLDPE | MarFlex® |
| Vi-Chem PVC V145-70E | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Chiao Fu PA66/6 MB312GM33 BK | Chiao Fu Enterprises Co., Ltd. | Nylon 66/6 | Chiao Fu PA66/6 |
| Kingfa PP-R2 | Kingfa | PP, Unspecified | Kingfa |
| HiPrene® HT42 | GS Caltex | PP, Unspecified | HiPrene® |