LNP™ STAT-KON™ DX04490 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PNL3SD_LNP-STAT-KON-DX04490-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON DX04490 is a compound based on Polycarbonate resin containing Proprietary Filler(s). Added feature of this grade is: Electrically Conductive. Also known as: LNP* STAT-KON* Compound PDX-D-04490 Product reorder name: DX04490 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hr | 0.40 | % | ASTM D955 |
| Across Flow : 24 hr | 0.50 | % | ASTM D955, ISO 294-4 |
| Flow : 24 hr | 0.42 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2990 | MPa | ASTM D638 |
| -- | 2720 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 60.7 | MPa | ASTM D638 |
| Yield | 61.1 | MPa | ISO 527-2 |
| Break | 53.8 | MPa | ASTM D638 |
| Break | 54.3 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 4.2 | % | ASTM D638 |
| Yield | 4.5 | % | ISO 527-2 |
| Break | 16 | % | ASTM D638 |
| Break | 8.5 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 2720 | MPa | ASTM D790 |
| -- | 2510 | MPa | ISO 178 |
| Flexural Strength | |||
| -- | 89.6 | MPa | ASTM D790 |
| -- | 75.7 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 48 | J/m | ASTM D256 |
| 23°C 2 | 5.5 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 2300 | J/m | ASTM D4812 |
| 23°C 3 | 170 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 4.26 | J | ASTM D3763 |
| -- | 9.43 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 132 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 4 | 134 | °C | ISO 75-2/Af |
| CLTE | |||
| Flow : -40 to 40°C | 6.3E-5 | cm/cm/°C | ASTM E831 |
| Flow : -40 to 40°C | 6.4E-5 | cm/cm/°C | ISO 11359-2 |
| Transverse : -40 to 40°C | 5.9E-5 | cm/cm/°C | ASTM E831 |
| Transverse : -40 to 40°C | 6.1E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 to 1.0E+5 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 to 1.0E+5 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALAMID® 6.6 S NATUR-9142 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 66 | ALAMID® |
| Generic PESU - Carbon Fiber | Generic | PESU | Generic |
| Kazan LDPE 16214-020 OKP 22 111 3401 | Kazanorgsintez Joint Stock Company | LDPE | Kazan LDPE |
| Sylvin 8878-80 Brown 7380 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| ULTEM™ 1100 resin | SABIC Innovative Plastics | PEI | ULTEM™ |