Adell Polyamide AR-34
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Adell Plastics, Inc. |
| Trademark: | Adell Polyamide |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PMfkfL_Adell-Polyamide-AR-34.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Adell Polyamide AR-34 is a polyamide 66 (nylon 66) material, which contains a 20% glass fiber reinforced material. This product is available in North America,. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.23 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 - 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | ASTM D785 | ||
| Class m | 96 | ASTM D785 | |
| Class r | 121 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 124 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 7580 | MPa | ASTM D790 |
| Flexural Strength | 214 | MPa | ASTM D790 |
| Compressive Strength | 207 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 75 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 238 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 227 | °C | ASTM D648 |
| Melting Temperature | 254 - 271 | °C |
| Additional Information |
|---|
| DTUL @ 66 psi, ASTM D648: >480°FElongation at Break, ASTM D638: 3 to 4%Specific Gravity, ASTM D792: 1.22 to 1.24 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMIKASUPER® LCP E6809T | Sumitomo Chemical Co., Ltd. | LCP | SUMIKASUPER® LCP |
| NANCAR® 1042 | Nantex Industry Co., Ltd. | NBR | NANCAR® |
| HI-ZEX™ 530M | Prime Polymer Co., Ltd. | HDPE | HI-ZEX™ |
| KRYSTALFLEX™ PE429 | Huntsman Corporation | PUR-Eth,aliphat | KRYSTALFLEX™ |
| LNP™ LUBRICOMP™ WL0049 compound | SABIC Innovative Plastics | PBT | LNP™ LUBRICOMP™ |