Braskem EVA TN2006
| Category: | EVA , Ethylene Vinyl Acetate Copolymer |
| Manufacturer: | Braskem |
| Trademark: | Braskem EVA |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PM3iB6_Braskem-EVA-TN2006.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TN2006 is an Ethylene-Vinyl Acetate (EVA) copolymer with good mechanical properties, high flexibility and toughness even with low temperature, excellent optical and salability properties. Additionally, this product has good water vapor barrier. The melt properties allow processability in tubular film equipment, being able to be coextruded in combination with many others materials |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.940 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Vinyl Acetate Content | 18.0 | wt% |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, Compression Molded | 89 | ||
| Shore D, Compression Molded | 39 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 33.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, Compression Molded) | 680 | % | ASTM D638 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Secant Modulus | ASTM D882 | ||
| 2% Secant, MD : 50 µm, Blown Film | 39.0 | MPa | |
| 2% Secant, TD : 50 µm, Blown Film | 38.0 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 32.0 | MPa | |
| TD : Break, 50 µm, Blown Film | 31.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm, Blown Film | 450 | % | |
| TD : Break, 50 µm, Blown Film | 700 | % | |
| Dart Drop Impact (50 µm, Blown Film) | 600 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 50 µm, Blown Film | 150 | g | |
| TD : 50 µm, Blown Film | 350 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 70.0 | °C | ASTM D1525 1 |
| Peak Melting Temperature | 90.0 | °C | ASTM D3418 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.0 µm, Blown Film) | 87 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | 1.3 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 1 (10 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 4MID® 9A22325 | 4Plas | Nylon 66 | 4MID® |
| Alkathene® Ultra LDJ225 | Qenos Pty Ltd | LLDPE | Alkathene® Ultra |
| Axiall PVC 7140 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Hangzhou Keli ACS C-130F | Hangzhou Keli Chemical Co., Ltd. | ACS | Hangzhou Keli ACS |
| StarPet® 8015-0000 | Star Thermoplastic Alloys & Rubbers, Inc. | TPE | StarPet® |