Elastocon® STK60B black thermoplastic elastomer has been developed for applications that require ultra soft rubber-like properties and a good surface finish. Elastocon® STK60B is well suited for consumer goods and industrial applications requiring non-slip/soft touch ergonomics, sound and vibration dampening, improved impact resistance, and U.V. stability. Elastocon® STK60B can be overmolded to polycarbonate, ABS, PC/ABS, Acrylic, HIPS, and various grades of nylon 6 and Nylon 6/6.

General Information
Features	Shock absorption Noise reduction Impact resistance, good Good UV resistance Soft Excellent appearance
Uses	overmolding Industrial application Consumer goods application field
Appearance	Black
Forms	Particle
Processing Method	Blow molding Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.920	g/cm³	ASTM D792

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	64		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (100% Strain)	1.80	MPa	ASTM D412
Tensile Strength (Yield)	8.30	MPa	ASTM D412
Tensile Elongation (Break)	570	%	ASTM D412

Injection	Nominal Value	Unit
Rear Temperature	210 - 216	°C
Front Temperature	216 - 266	°C
Nozzle Temperature	227 - 277	°C
Mold Temperature	27.0 - 49.0	°C
Back Pressure	0.520 - 1.21	MPa

Injection instructions
Elastocon® thermoplastic elastomers are shear dependent and have been formulated to process on conventional thermoplastic equipment for injection molding, extrusion or blow molding. Our tests have shown that overmolding onto a non-gloss, matte surface finish will help optimize overmold adhesion to the substrate. Be sure to incorporate mechanical interlocks and 1:1 through holes whenever possible when designing two shot components. Feathered edges should always be avoided to ensure adequate and consistant shut off against the substrate, while also eliminating exposed tapered edges that can be subject to adhesive failure.Injection Rate: 1 to 5 in/sec

Injection instructions

Elastocon® thermoplastic elastomers are shear dependent and have been formulated to process on conventional thermoplastic equipment for injection molding, extrusion or blow molding. Our tests have shown that overmolding onto a non-gloss, matte surface finish will help optimize overmold adhesion to the substrate. Be sure to incorporate mechanical interlocks and 1:1 through holes whenever possible when designing two shot components. Feathered edges should always be avoided to ensure adequate and consistant shut off against the substrate, while also eliminating exposed tapered edges that can be subject to adhesive failure.Injection Rate: 1 to 5 in/sec

Resin Grade	Manufacturer	Category	Trademark
PureTherm® 1003C	Tekni-Films, a div of Tekni-Plex	Film, PVC	PureTherm®
Supol HT121E	LyondellBasell Industries	PP Copolymer	Supol
Electrafil® PC 03906 MB	Techmer Engineered Solutions	PC	Electrafil®
Huaxia Shenzhou FKM DS2601-1	Shandong Huaxia Shenzhou New Material Co., Ltd.	Fluorelastomer	Huaxia Shenzhou
MAJORIS POLYPROPYLENE 30 MS NOIR 8229	AD majoris	PP, Unspecified	MAJORIS