EvoSource™ ABS 4535 70/05
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | MBA Polymers |
| Trademark: | EvoSource™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PKldAY_EvoSource-ABS-4535-70-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A UL-HB recognized, easy flowing, post-consumer recycled acrylonitrile-butadiene-styrene copolymer for general use. Available in mouse grey (reference 70/05). |
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.07 | g/cm³ | Internal Method |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 24 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 41.0 | MPa | ISO 527-2/50 |
| Flexural Modulus (23°C) | 2400 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact Strength (23°C) | 13 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 92.0 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | ASTM D257 |
| High Amp Arc Ignition (HAI) (1.50 to 2.80 mm) | PLC 1 | UL 746 | |
| Hot-wire Ignition (HWI) 1(1.50 to 2.80 mm) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 to 2.80 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Processing (Melt) Temp | 210 to 250 | °C | |
| Mold Temperature | 40.0 to 60.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Melt Temperature | 200 to 220 | °C |
| Note Message | |
|---|---|
| 1 . | ASTM D 3847 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safron® H500-25RG | Safripol (PTY) LTD | PP Homopolymer | Safron® |
| Sinvicomp SRF3705 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Rigid | Sinvicomp |
| ULTEM™ foam DU319 | SABIC Innovative Plastics Asia Pacific | PEI | ULTEM™ foam |
| Utomer UT380 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyester | Utomer |
| Polidan® PNT 0553/23 | Solvay Specialty Polymers | XLPE | Polidan® |