KumhoSunny PBT 3710FG
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Shanghai KumhoSunny Plastics Co., Ltd. |
| Trademark: | KumhoSunny PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PIYrdO_KumhoSunny-PBT-3710FG.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT3710FG is 10%GF reinforced flame retardant PBT resin. PBT3710FG has high rigidity, super shape resistance property, high heat resistance and excellent UV stability. PBT3710FG is mainly used in electric connector, compress system ending,power tools housing, communication equipment, sports equipments, etc. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.46 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 80.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 8.0 | % | ASTM D638 |
| Flexural Modulus | 4000 | MPa | ASTM D790 |
| Flexural Strength | 130 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 55 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 200 | °C | |
| 1.8 MPa, Unannealed | 170 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 140 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 220 to 240 | °C | |
| Middle Temperature | 230 to 250 | °C | |
| Front Temperature | 240 to 260 | °C | |
| Nozzle Temperature | 240 to 260 | °C | |
| Processing (Melt) Temp | 220 to 250 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.200 to 0.800 | MPa | |
| Screw Speed | 20 to 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-FR-UV2 | Polymer Resources Ltd. | PC | PRL |
| RJM SI302G15 | RJM International, Inc. | PET | RJM |
| Taitalac® 6003 | Taita Chemical Company, Ltd. | ABS | Taitalac® |
| Sylvin 802-85 CLEAR BLUE 841 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Multilon® TN-7570Z | TEIJIN LIMITED | PC+ABS | Multilon® |