Grilon® TSG-60/4 W
| Category: | Nylon 66/6 , Polyamide 66/6 Copolymer |
| Manufacturer: | EMS-GRIVORY |
| Trademark: | Grilon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PDga6p_Grilon-TSG-60-4-W.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Grilon® TSG-60/4 W is a Polyamide 66/6 Copolymer (Nylon 66/6) material filled with 60% glass fiber. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Grilon® TSG-60/4 W are:
Typical applications include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.72 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.30 | -- | % | |
| Flow | 0.10 | -- | % | |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 5.0 | -- | % | |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 317 | 198 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20000 | 13000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 242 | 159 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.2 | 3.6 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 12 | 11 | kJ/m² | |
| 23°C | 13 | 18 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 86 | 76 | kJ/m² | |
| 23°C | 86 | 91 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 1.8 MPa, Unannealed | 245 | -- | °C | ISO 75-2/A |
| 8.0 MPa, Unannealed | 210 | -- | °C | ISO 75-2/C |
| Continuous Use Temperature | Internal Method | |||
| -- 1 | 130 to 150 | -- | °C | |
| -- 2 | 230 | -- | °C | |
| Melting Temperature 3 | 265 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.3E-5 | -- | cm/cm/°C | |
| Transverse | 8.7E-5 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification (0.800 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA 66+PA 6, MHR, 14-160 N, GF 60 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | Long Term |
| 2 . | Short Term |
| 3 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 TC-C-25 | RTP Company | Nylon 66 | RTP |
| Restramid PA 6 50GF | Polimarky Spolka Jawna | Nylon 6 | Restramid |
| Sindustris PBT SV1121M | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| VITAMIDE® BG35BK6357 | Jackdaw Polymers | Nylon 6 | VITAMIDE® |
| Halene P F103 | Haldia Petrochemicals Ltd. | PP Homopolymer | Halene P |