ULTEM™ foam XP080
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | ULTEM™ foam |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PDa6ox_ULTEM-foam-XP080.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ULTEM foam is a polyetherimide based thermoplastic foam with excellent flame, smoke and toxicity performance. The material combines a high strength to weight ratio with low moisture absorption. The foam also possesses excellent dielectric properties. ULTEM foam is targeted at applications where structural fire performance, radar transparency, or extreme hot or cold environments are required. ULTEM foam is thermoformable and compatible with phenolic pre-pregs. Information on processing or secondary operations is available upon request. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.0800 | g/cm³ | ASTM D1622 |
| Water Absorption (Equilibrium) | 4.0 | % | ASTM D272 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 37.0 | MPa | ASTM D638 |
| Tensile Strength 2 | 1.70 | MPa | ASTM D638 |
| Compressive Modulus 3 | 71.0 | MPa | ASTM D1621 |
| Compressive Strength 4 | 1.20 | MPa | ASTM D1621 |
| Shear Modulus | 19.0 | MPa | ASTM C273 |
| Shear Strength | 1.00 | MPa | ASTM C273 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Unnotched Impact Strength | 0.80 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermal Conductivity | 0.037 | W/m/K | ASTM C518 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Insulation Radiant Panel | PASSES | FAR 25.853 | |
| OSU Peak Heat Release Rate 5 | < 55.0 | kW/m² | FAR 25.853 |
| OSU Total Heat Release 6 | < 55.0 | kW·min/m² | FAR 25.853 |
| Smoke Density | < 10 | Ds | FAR 25.853 |
| Smoke Toxicity | Internal Method | ||
| OEM ABD | PASSES | ||
| OEM BSS | PASSES | ||
| Vertical Burn - 60 second | PASSES | FAR 25.853 |
| Note Message | |
|---|---|
| 1 . | In plane |
| 2 . | In plane |
| 3 . | Perpendicular to plane |
| 4 . | Perpendicular to plane |
| 5 . | 5 minute test |
| 6 . | 2 minute test |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Polypropylene F56-01 | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| TECHNO ABS 810 | Techno Polymer Co, Ltd. | ABS | TECHNO ABS |
| Next Nylon 66 Prime Series PG33-01ABK | Next Polymers Ltd. | Nylon 66 | Next Nylon 66 Prime Series |
| ADDILENE J 520 M20 | ADDIPLAST | PP Copolymer | ADDILENE |
| Lucky Enpla LPC1000 | Lucky Enpla Co LTD | PC | Lucky Enpla |