Kingfa HC-110
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Kingfa |
| Trademark: | Kingfa |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | PALcgG_Kingfa-HC-110.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Kingfa HC-110 is an acrylonitrile butadiene styrene (ABS) material,. This product is available in North America or Asia Pacific region. The processing method is injection molding. The main characteristics of Kingfa HC-110 are: flame retardant/rated flame. The typical application field of Kingfa HC-110 is: automobile industry |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 200°C/5.0 kg | 1.8 | g/10 min | ASTM D1238 |
| 220°C/10.0 kg | 20 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.40 - 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 100 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 44.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 25 | % | ASTM D638 |
| Flexural Modulus 3 | 2200 | MPa | ASTM D790 |
| Flexural Strength 4 | 66.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| 23°C, 3.20 mm | 330 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 300 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 96.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 87.0 | °C | ASTM D648 |
| Vicat Softening Temperature | |||
| -- | 103 | °C | ASTM D1525 5 |
| -- | 95.0 | °C | ASTM D1525 6 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength | 23 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 90.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 182 - 205 | °C | |
| Middle Temperature | 205 - 230 | °C | |
| Front Temperature | 215 - 240 | °C | |
| Processing (Melt) Temp | 220 - 245 | °C | |
| Mold Temperature | 30.0 - 60.0 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.00 - 0.0100 | MPa |
| Injection instructions |
|---|
| Processing Temperature Limit: 250°C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 2.0 mm/min |
| 4 . | 2.0 mm/min |
| 5 . | 标准 B (120°C/h), 压 力1 (10N) |
| 6 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2199 X 133082 B | RTP Company | PEI | RTP |
| Regis® 6015 | Noble Polymers | Polyolefin, Unspecified | Regis® |
| Norpex® PPE AX235 | Custom Resins Group | PPE | Norpex® |
| Nipol® 1031 | Zeon Chemicals L.P. | NBR | Nipol® |
| Lotader® 4700 | Arkema | EEA | Lotader® |