Karina BLACK PVC COMPOUND 601-48/ 1-BY-IS-BZ
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | P9vSal_Karina-BLACK-PVC-COMPOUND-601-48-1-BY-IS-BZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE, WEATHER RESISTANT PVC COMPOUND RECOMMENDED FOR INJECTION AND EXTRUSION OF AUTOMOTIVE PROFILES. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity 1 | 1.25 to 1.31 | g/cm³ | ASTM D792 |
| Color | OK | ME 12 | |
| Color a | -0.860 to 0.740 | ME 12 | |
| Color b | -1.02 to 0.580 | ME 12 | |
| Color L | 25.4 to 27.0 | ME 12 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | |||
| Shore A, 15 sec | 58 to 62 | ASTM D2240 | |
| Shore A, 15 sec 2 | 58 to 62 | TL VW 676 Part 3.1.1/3.1.2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Break, 80°C 3 | > 4.90 | MPa | TL VW 676 Part 3.4.2 |
| -- | > 4.90 | MPa | ASTM D638 |
| Tensile Elongation (Yield) | > 200 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation 4(Break) | > 200 | % | TL VW 676 Part 3.5.2 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged for 48 hr at 80°C |
| 3 . | 48 hr |
| 4 . | Aged for 48 hr at 80°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 2281 HF | RTP Company | PEEK | RTP |
| TAROLOX 10 G2 X0 | Taro Plast S.p.A. | PBT | TAROLOX |
| Weifang Kingdom CPE135A | Weifang Kingdom Plastic Co., Ltd | CPE | Weifang Kingdom |
| GAPEX® HT RNP23LB03BK | Ferro Corporation | Nylon+PP | GAPEX® HT |
| PHOENIX™ 8901 | Phon Tech Industrial Company | TPE | PHOENIX™ |